Influence of Heat Treatment and Magnesium Content on Corrosion Resistance of Al-Mg Coated Steel Sheet

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of heat treatment on microstructural properties of three-layer sheet aluminum magnesium - aluminum - stainless steel

Metal coating, metal materials are of two or more layers. The coating metals are widely used in industry. These sheets or saving performance and cost effective solution or both the user. Performance coating metals according to usage in structural applications, settings thermal expansion of the thermo-mechanical control (thermostat), electrical, magnetic, corrosion resistant, flowering and decor...

متن کامل

Cut-edge corrosion study on Al-rich metallic coated steel

Aluminium additions to metallic coatings on steel substrates have been accepted as a successful solution versus the standard zinc based coatings. The development of these products responds to the market’s demand of more versatile products, which faces the leaching effect of zinc and the rising cost of obtaining this element, among the main advantages. However, these materials show a special sen...

متن کامل

Corrosion Resistance of the Superhydrophobic Mg(OH)2/Mg-Al Layered Double Hydroxide Coatings on Magnesium Alloys

Coatings of the Mg(OH)2/Mg-Al layered double hydroxide (LDH) composite were formed by a combined co-precipitation method and hydrothermal process on the AZ31 alloy substrate in alkaline condition. Subsequently, a superhydrophobic surface was successfully constructed to modify the composite coatings on the AZ31 alloy substrate using stearic acid. The characteristics of the composite coatings wer...

متن کامل

The Effect of Heat Treatment on the Sensitized Corrosion of the 5383-H116 Al-Mg Alloy

In this study, the effects of heat treatment and sensitized corrosion on the 5383-H116 Al-Mg alloy were investigated for temperatures ranging from 100 to 450 °C. The results show that the heat treatment temperature is the main factor that causes changes to the microstructure and mechanical strength of the 5383-H116 Al-Mg alloy, inducing β-phase (Al₃Mg₂) precipitation in the form of a continuous...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Journal of the Korean institute of surface engineering

سال: 2016

ISSN: 1225-8024

DOI: 10.5695/jkise.2016.49.2.202