Influence of Bond Coat Roughness on Life Time of APS Thermal Barrier Coating Systems under Thermo-Mechanical Load
نویسندگان
چکیده
منابع مشابه
AN INVESTIGATION ON EFFECT OF BOND COAT REPLACEMENT ON HOT CORROSION PROPERTIES OF THERMAL BARRIER COATINGS
In the present study NiCrAlY bond coating layer was produced by electroplating against common atmospheric plasma spraying (APS). Both types of the bond coats were applied on IN738LC base metal then, the YSZ (ZrO2-8% Y2O3) thermal barrier top layer was coated by atmospheric plasma spray technique. Hot corrosion is one of the main destructive factors in thermal barrier coatings (TBCs) which come ...
متن کاملInfluence of Setting Time of Tack Coat on Bond Strength of Bituminous Paving Layers
Poor adhesion between two successive bituminous layers causes adverse effects on the structural strength of the pavement and develops a numbers of premature failure. To improve the adhesion, it is a general practice to apply a tack coat over an existing or newly constructed bituminous surface before laying another bituminous layer. The main objective of this study is to explore the influence of...
متن کاملThermo-mechanical analysis of a coated cylinder head
This paper presents finite element analysis (FEA) of a coated and uncoated cylinder heads of a diesel engine to examine the distribution of temperature and stress. A thermal barrier coating system was applied on the combustion chamber of the cylinder heads, consists of two-layer systems: a ceramic top coat (TC), made of yttria stabilized zirconia (YSZ), ZrO2-8%Y2O3 and also a metallic bond coat...
متن کاملThermal Fatigue Behavior of Air-Plasma Sprayed Thermal Barrier Coating with Bond Coat Species in Cyclic Thermal Exposure
The effects of the bond coat species on the delamination or fracture behavior in thermal barrier coatings (TBCs) was investigated using the yclic thermal fatigue and thermal-shock tests. The interface microstructures of each TBC showed a good condition without cracking or delamination after flame thermal fatigue (FTF) for 1429 cycles. The TBC with the bond coat prepared by the air-plasma spray ...
متن کاملa study on the numerical simulation of thermo-mechanical behavior of the novel functionally graded thermal barrier coating under thermal shock
an attempt was made to investigate the thermal and residual stress distribution in a novel three layer (la 2 zr 2 o 7 / 8ysz/ nicraly) during a real-like heating regime which includes heating, service time and final cooling. for achieving maximum accuracy and consistency in calculation of thermal and mechanical properties of hybrid coating system, all related andrequired properties were introdu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Solid Mechanics and Materials Engineering
سال: 2010
ISSN: 1880-9871
DOI: 10.1299/jmmp.4.208