Influence of B2O3and Basicity on Viscosity and Structure of Medium Titanium Bearing Blast Furnace Slag
نویسندگان
چکیده
منابع مشابه
PROCESSING OF TiO2 FROM TITANIUM-BEARING BLAST FURNACE SLAG AS TITANIUM SOURCE
X. Li, H.H. Yu, Z. H. Fang, Z. G. Yuan, School of Material Science and Engineering, Shenyang Ligong University, Shenyang, China; X. X. Xue, School of Material and Metalurgy, Northeastern University, Shenyang, China The titanium dioxide(TiO2) was prepared by efficient decomposition of titaniumbearing blast furnace slag (TBBFS) in molten salt system. The as-prepared TiO2 were characterized by X-r...
متن کاملGround Granulated Blast Furnace Slag
1. Ground Granulated Blast Furnace Slag Ground Granulated Blast Furnace Slag (GGBFS) is a by product of the steel industry. Blast furnace slag is defined as “the non-metallic product consisting essentially of calcium silicates and other bases that is developed in a molten condition simultaneously with iron in a blast furnace.” [1] In the production of iron, blast furnaces are loaded with iron o...
متن کاملEFFECTS OF SILICA MODULUS AND ALKALI CONCENTRATION ON ACTIVATION OF BLAST-FURNACE SLAG
Abstract: The use of alkali-activated cementitious materials especially over the past decades has significantly been increased. The goal of this research is to investigate the effects of silica modulus and alkali concentration on alkali-activation of blast-furnace slag. In this research, the most important physical characteristics of cementitious systems, i.e. the 28-day compressive strength...
متن کاملThe Study of Ion Adsorption by Amorphous Blast Furnace Slag
In this study, the blast furnace slag was used as absorbing bed and then, its ionic adsorption was studied. For this reason, various experimental parameters such as pH, contact time and the primary ion concentration were investigated. The remaining concentrations of ions such as; Mn2+ and Fe2+ in water were measured by atomic adsorption spectroscopy. The chemical and p...
متن کاملOxidation Kinetics and Oxygen Capacity of Ti-Bearing Blast Furnace Slag under Dynamic Oxidation Conditions
Li Zhang 1,*, Wu Zhang 2, Juhua Zhang 3 and Guangqiang Li 3 1 School of Materials and Metallurgy, Northeastern University, Shenyang 110819, China 2 School of Materials Science and Engineering, Shenyang Ligong University, Shenyang 110168, China; [email protected] 3 The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China; zhangj...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Chemistry
سال: 2016
ISSN: 2090-9063,2090-9071
DOI: 10.1155/2016/6754593