Influence of Al on glass forming ability and nanocrystallization behavior of cast-iron based bulk amorphous alloy
نویسندگان
چکیده
منابع مشابه
KINETICS OF -Fe NANOCRYSTALLIZATION IN Fe55Cr18Mo7B16C4 BULK AMORPHOUS ALLOY
Abstract: In this research work, crystallization kinetics of Fe55Cr18Mo7B16C4 alloy was evaluated by X-ray diffraction, TEM observations and differential scanning calorimetric tests. In practice, crystallization and growth mechanisms were investigated using DSC tests in four different heating rates. Results showed that a two -step crystallization process occurred in the alloy in which - Fe phas...
متن کاملNANOCRYSTALLIZATION MECHANISMS OF Fe52Cr18Mo7B16C4Nb3 BULK AMORPHOUS STEEL
Crystallization kinetics of Fe52Cr18Mo7B16C4Nb3 alloy was evaluated using X-ray diffraction, differential scanning calorimetric (DSC) tests and TEM observations in this research work. In effect, crystallization and growth mechanisms were investigated using DSC tests in four different heating rates (10, 20, 30, 40 K/min) and kinetic models (i.e. Kissinger- Starink, Ozawa, and Matusita methods). ...
متن کاملUnusual glass-forming ability of bulk amorphous alloys based on ordinary metal copper.
We report the unusual glass-forming ability (GFA) of a family of Cu-based alloys, Cu46Zr47-xAl7Yx (0<x< or =10, in at. %), and investigate the origin of this unique property. By an injection mold casting method, these alloys can be readily solidified into amorphous structures with the smallest dimension ranging from 4 mm up to 1 cm without detectable crystallinity. Such superior GFA is found pr...
متن کاملGlass Forming Ability and Corrosion Resistance of Zr-Cu-Ni-Al-Ag Bulk Metallic Glass
Zr70−xCu12.5Ni10Al7.5Agx (x = 0–10) bulk metallic glasses (BMGs) have been prepared by copper mold casting. The glass-forming ability (GFA) and corrosion behavior of Zr-based BMGs have been investigated. It is found that the GFA of Zr-based BMGs first increases and then decreases with the increase of the Ag content, and the best glass former is Zr65Cu12.5Ni10Al7.5Ag5 with the maximum thickness ...
متن کاملNanocrystallization in Co67Cr7Fe4Si8B14 Amorphous Alloy Ribbons
The nanocrystallization of Co67Fe4Cr7Si8B14 amorphous ribbons which prepared by planar flow melt spinning process (PFMS) was investigated. Crystallization of the ribbons was studied by differential thermal analysis (DTA), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The DTA result of amorphous ribbon at heating rate of 10˚C/min showedoccurrence of phase transitions in two...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Research
سال: 2015
ISSN: 0884-2914,2044-5326
DOI: 10.1557/jmr.2015.48