Induced magnetic anisotropy and thickness dependence of magnetic properties in nanocrystalline alloy "finemet".
نویسندگان
چکیده
منابع مشابه
Magnetic Properties of Ni0.3Fe0.7 Alloy Nanowires
The effect of length variation on the magnetic properties of NiFe alloy nanowires electrodeposited into the alumina template was investigated. The diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. Energy dispersive spectroscopy results showed Ni3Fe7 composition of the alloy nanowire...
متن کاملMagnetic and Electrical Properties of Nanocrystalline Fe85Si10Ni5/Phenolic Resin Soft Magnetic Composites
In this work, nanocrystalline Fe85Si10Ni5 soft magnetic powders were prepared by mechanical alloying and subsequent annealing to reduce the internal stresses and lattice strains. The powders were mixed with phenolic resin and warm pressed to produce nanostructured soft magnetic composites. The effect of annealing time and temperature on the crystalline structure, microstructure and magnetic pro...
متن کاملMagnetic Properties and Crystallization Kinetics of a Mn-Doped FINEMET Precursor Amorphous Alloy
The kinetics of nanocrystallization of a Mn-doped FINEMET alloy from its amorphous precursor is reported. The alloy studied was of a composition (Fe1 Mn )73 5Nb3CuSi13 5B9 where = 0 05. X-ray diffraction (XRD) confirmed that -FeSi is the product of primary nanocrystallization. Crystallization kinetics were studied using time-dependent magnetization, ( ), as a measure of the volume fraction crys...
متن کاملDC bias immune nanocrystalline magnetic cores made of Fe73Nb3Cu1B7Si16 ribbon with induced transverse magnetic anisotropy
The comparative analysis of magnetic properties of cut cores made of nanocrystalline Fe73Nb3Cu1B7Si16 alloy ribbon and cores made of the same ribbon with preliminary tension-induced transverse magnetic anisotropy was carried out. The possibility of improving magnetic properties of cut cores, decreasing loss, and increasing DC bias immunity of reversible magnetic permeability is presented. The i...
متن کاملبررسی سینتیک نانو تبلور نوارهای نرم مغناطیس FINEMET در شرایط غیرهمدما
The soft magnetic nanocrystalline Fe73.5Si13.5B9Cu1Nb3 alloy (FINEMET®) is produced by heat treatment of amorphous precursor. Determining kinetic parameters of amorphous structure transformation to nanocrystalline allows the control of microstructure (e.g. size and volume fraction of nanocrystalline grains) in order to achieve desired soft magnetic properties by optimizing the heat treatment co...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 1990
ISSN: 0285-0192
DOI: 10.3379/jmsjmag.14.193