In Vitro Corrosion Behaviour of Ti–6Al–4V and 316L Stainless Steel Alloys for Biomedical Implant Applications
نویسندگان
چکیده
منابع مشابه
Passivation and corrosion behaviours of AISI 316L stainless steel as implant materials in simulated blood environment
The purpose of the study was evaluation of corrosion resistance of steel 316L used in cardiologic treatment mainly for vascular stents. The study analysed influence of electrochemical and chemical treatment of the steel surface, including sterilisation with pressurised water steam, on its corrosion characteristics. The tests were performed in artificial blood plasma simulating human blood envir...
متن کاملMicro abrasion-corrosion of AISI 316L stainless steel
In this study, the synergistic effects of abrasion and corrosion on AISI 316L stainless steel have been investigated using a micro-abrasion test rig. A series of results from abrasioncorrosion tests conducted using the micro-abrasion rig are presented. AISI 316L stainless steel has been studied under both pure abrasion and abrasion-corrosion conditions simulated by either distilled water or 3.5...
متن کاملDetermination of susceptibility to intergranular corrosion and electrochemical reactivation behaviour of AISI 316L type stainless steel
In this study, double loop electrochemical potentiokinetic reactivation (DLEPR) test was applied to determine the degree of sensitization in 316L type stainless steel, where obtained results were correlated with revealed microstructures after oxalic acid test and weight loss measurements of Streicher and Huey acid tests. Best agreement was provided with test parameters which are 1 M H2SO4 and 0...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Bio- and Tribo-Corrosion
سال: 2017
ISSN: 2198-4220,2198-4239
DOI: 10.1007/s40735-017-0118-8