Improving the Mechanical Properties of a Car Bumper by Using Glass Fiber Reinforced Composite Laminates and Nano-ceramic Filler
نویسندگان
چکیده
In this study, mechanical tests were performed on a Chinese car bumper of the Chery model, which was chosen for examination due to its widespread use in Iraqi streets. It also compared best specimens obtained these study stages. Glass fiber mats and nanoparticles have been mixed with unsaturated polyester resin (UPE) two first stage, fibers volume fraction 14% properties calculated. second different weight fractions zirconium oxide (ZrO2) added mixture, recalculated. The experimental test's results illustrated that tensile strength, fracture toughness, damping ratio composite material enhanced when mixing vf glass by about (285.85%, 207.56%, 100%) respectively, bumper, while impact resistance decreased (-24.55%). same repeated after adding (1%, 2%, 2.5%, 3%, 3.5%, 4%) it observed had significant effect since at first, improved them until reached 2.5 wt.%, but any higher addition than caused decrease enhancement properties. Thus, found wt.% gave us improvement resistance, (436.32%, 47.28%, 438.66%, 52.3%)
منابع مشابه
Evaluation of Mechanical and Tribological Properties of Glass/Carbon Fiber Reinforced Polymer Hybrid Composite
Polymer matrix composites used in different industrial applications due to their enhanced mechanical properties and lightweight. However, these materials are subjected to friction and wear situations in some industrial and automobile applications. Therefore, there is a need to investigate the wear properties of polymer matrix composite materials. This article emphasizes the dry abrasive wear be...
متن کاملMECHANICAL PROPERTIES OF DENTAL COMPOSITE MATERIALS REINFORCED WITH MICRO AND NANO-SIZE Al2O3 FILLER PARTICLES
Abstract: Composite specimens were prepared by dispersion of various amounts of nano-sized Al2O3 fillers in a monomer system containing 60% Bis-GMA and 40% TEGDMA. For comparative purposes, composite samples containing micrometer size Al2O3 fillers were also prepared following the same procedure. The mechanical properties of the light- cured samples were assessed by three-point flexural strengt...
متن کاملMECHANICAL PROPERTIES OF DENTAL COMPOSITE MATERIALS REINFORCED WITH MICRO AND NANO-SIZE Al2O3 FILLER PARTICLES
Composite specimens were prepared by dispersion of various amounts of nano-sized Al2O3 fillers in a monomer system containing 60% Bis-GMA and 40% TEGDMA. For comparative purposes, composite samples containing micrometer size Al2O3 fillers were also prepared following the same procedure. The mechanical properties of the lightcured samples were assessed by three-point flexural strength, diametral...
متن کاملEnvironmental Effects on Mechanical Properties of Glass/Epoxy and Fiber Metal Laminates, Part I: Hygrothermal Aging
In this article, the effect of hygrothermal aging on mechanical properties of fiber metal laminates (FMLs) and E-glass/epoxy (GE) composites is investigated. First, FML and GE specimens were built using wet lay-up technique under vacuum pressure. Hygrothermal aging simulation was then carried out on both specimen types in distilled water at a constant temperature of 90 °C for 5 weeks. The resul...
متن کاملEnvironmental effects on mechanical properties of glass/epoxy and fiber metal laminates, Part II: Isothermal aging
The aim of this study is to investigate effects of isothermal aging on mechanical properties of fiber metal laminates (FMLs) and glass/epoxy composites. For this purpose, both materials were fabricated using the wet lay-up manufacturing technique under vacuum pressure. Both the glass/epoxy composites and the FML specimens were then subjected to isothermal aging (130°C, dried air) for up to 5 we...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Iraqi journal of industrial research
سال: 2022
ISSN: ['2788-712X']
DOI: https://doi.org/10.53523/ijoirvol9i2id189