Improvement of O2 adsorption for α-MnO2 as an oxygen reduction catalyst by Zr4+ doping
نویسندگان
چکیده
منابع مشابه
Electrodeposition of platinum nanoparticles on reduced graphene oxide as an efficient catalyst for oxygen reduction reaction
Reduced graphene oxide film was synthesized on a glassy carbon electrode by electro reduction of graphene oxide powders in aqueous solution. Then platinum nano particles were deposited on reduced graphene oxide film that was deposited on the glassy carbon electrode via electro reduction of platinum salt. The Physical morphology of the platinum on reduced graphene oxide film was evaluated by sca...
متن کاملnano-rods zno as an efficient catalyst for the synthesis of chromene phosphonates, direct amidation and formylation of amines
چکیده ندارد.
Nanostructured porous RuO2/MnO2 as a highly efficient catalyst for high-rate Li-O2 batteries.
Despite the recent advancements in Li-O(2) (or Li-air) batteries, great challenges still remain to realize high-rate, long-term cycling. In this work, a binder-free, nanostructured RuO(2)/MnO(2) catalytic cathode was designed to realize the operation of Li-O(2) batteries at high rates. At a current density as high as 3200 mA g(-1) (or ∼1.3 mA cm(-2)), the RuO(2)/MnO(2) catalyzed Li-O(2) batteri...
متن کاملGraphene-Ni-α-MnO2 and -Cu-α-MnO2 nanowire blends as highly active non-precious metal catalysts for the oxygen reduction reaction.
Graphene-like carbon-Ni-α-MnO(2) and -Cu-α-MnO(2) blends can serve as effective catalysts for the oxygen reduction reaction with activities comparable to Pt/C.
متن کاملPreparation of Ag4Bi2O5/MnO2 Corn/Cob Like Nano Material as a Superior Catalyst for Oxygen Reduction Reaction in Alkaline Solution
Ag4Bi2O5/MnO2 nano-sized material was synthesized by a co-precipitation method in concentrated KOH solution. The morphology characterization indicates that MnO2 nanoparticles with a size of 20 nm are precipitated on the surface of nano Ag4Bi2O5, forming a structure like corn on the cob. The obtained material with 60% Mn offers slightly higher initial potential (0.098 V vs. Hg/HgO) and limiting ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: RSC Advances
سال: 2018
ISSN: 2046-2069
DOI: 10.1039/c7ra10079e