Improvement of Fatigue Limit by Shot Peening for High Strength Steel Specimens Containing a Crack-like Surface Defect
نویسندگان
چکیده
منابع مشابه
Side Effects of Shot Peening on Fatigue Crack Initiation Life
Shot peening beneficial effects on fatigue life of mechanical components are well known. However, there are some reports in the literature that indicate inappropriate shot peening parameters tend to reduce the fatigue life. It is therefore, the purpose of this study to find a logical quantitative justification for these observations. Using finite element method, a dynamic elastic-plastic simula...
متن کاملEvaluation of Fatigue Strength Improvement by CFRP Laminates and Shot Peening onto the Tension Flanges Joining Corrugated Steel Webs
Corrugated steel web with inherent high out-of-plane stiffness has a promising application in configuring large span highway bridge girders. Due to the irregularity of the configuration details, the local stress concentration poses a major fatigue problem for the welded flange plates of high strength low alloy structural steels. In this work, the methods of applying CFRP laminate and shot peeni...
متن کاملEffect of Residual Stresses on Fatigue Strength of Severely Surface Deformed Steels by Shot Peening
The compressive stress distribution below the specimen surface of severely surface deformed steels by shot peening was investigated by using laboratory X-rays and high-energy X-rays from a synchrotron radiation source, SPring-8 in the Japan Synchrotron Radiation Research Institute. Medium carbon steel plates were heat treated in two different conditions. The Vickers hardness of material-A and B...
متن کاملNumerical and Experimental Evaluation of Residual Stress and Fatigue Strength of Steel CK35 in Shot Peening Process
In shot peening process the work piece surface is struck by a large number of balls and compressive residual stress is generated on the surface. So, mechanical properties such as fatigue strength, stress corrosion resistance, smooth shape and ... will improve. In this paper, the balls with a speed of 100 to 200 m/s were struck on the steel samples and fatigue strength compared with specimens wi...
متن کاملShot Peening as an Alternative to Fatigue Life Improvement of CK45 Steel Coated with an Electroless Ni-Cu-P
The effect of an electroless Ni-Cu-P coating on the fatigue behavior of quenched and tempered CK45 steel has been investigated. The fatigue tests under rotating bending conditions have been conducted in three different conditions of uncoated, as-deposited and shot peened prior to the coating deposition. The results indicate that plating of the base steel leads to a fatigue life reduction. The d...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 2009
ISSN: 0514-5163,1880-7488
DOI: 10.2472/jsms.58.1030