Improved Thermal Cycling Durability of Thermal Barrier Coatings Manufactured by PS-PVD
نویسندگان
چکیده
منابع مشابه
Improved the Durability of Thermal Barrier Coatings with Interface Modified by ThreeDimensional Mesh Patterns
An approach to improve the lifetime of air plasma sprayed (APS) thermal barrier coatings (TBCs) by modifying the interfacial microstructure has been reported. The laser powder deposition technique was employed to fabricate the mesh structure (with the same composition as the bond coat) at the ceramic–substrate interface. After thermal cycling test, the APS TBCs with the mesh exhibited a much le...
متن کاملThermal Barrier Coatings – Durability Assessment and Life Prediction
Thermal barrier coating (TBC) systems are coating systems containing a metallic bond coat and a ceramic top coat. TBCs are used in gas turbines for thermal insulation and oxidation resistance. Life prediction of TBCs is important as high-temperature exposure degrades the coatings through mechanisms such as thermal fatigue and the formation and growth of thermally grown oxides (TGOs). This thesi...
متن کاملResidual Stresses of Eb-pvd Thermal Barrier Coatings Exposed to High Temperature
The substrate material was nickel-based superalloy (In738LC), and CoNiCrAlY was pressureless plasma-sprayed on the substrate as the bond coating. As the top coating, zirconia with 4 mol% yttria was electron beam-physical vapor deposited (EB-PVD) on the rotating substrate. The rotation speeds in the EB-PVD process were 5, 10 and 20rpm. The specimens were exposed to 1273K in air atmosphere for 20...
متن کاملErosion, Corrosion and Erosion-Corrosion of EB PVD Thermal Barrier Coatings
Electron beam (EB) physical vapour deposited (PVD) thermal barrier coatings (TBCs) have been used in gas turbine engines for a number of years. The primary mode of failure is attributed to oxidation of the bondcoat and growth of the thermally grown oxide (TGO), the alumina scale that forms on the bondcoat and to which the ceramic top coat adheres. Once the TGO reaches a critical thickness the T...
متن کاملsuppression of coke formation in thermal cracking by coke inhibitors
the main purpose of this research was to:1.develop a coking model for thermal cracking of naphtha.2.study coke inhibition methods using different coke inhibitors.developing a coking model in naphtha cracking reactors requires a suitable model of the thermal cracking reactor based on a reliable kinetic model.to obtain reliable results all these models shall be solved simultaneously.for this pu...
15 صفحه اولذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Thermal Spray Technology
سال: 2013
ISSN: 1059-9630,1544-1016
DOI: 10.1007/s11666-013-9971-2