Hydroxyapatite coating on AZ91 magnesium alloy via sol-gel method
نویسندگان
چکیده
منابع مشابه
Deposition of Nano-Crystalline Fluor-hydroxyapatite Coatings on Titanium Substrates via Sol-Gel Method
In this investigation, fluor-hydroxyapatite (FHA) film was deposited on a titanium substrate by sol-gel method. Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol solutions were used respectively as P, F and Ca precursors. Typical apatite structures were obtained for all coatings after dipping and subsequent heat treatment at 550, 700 and 800 ºC, the coating layers were ...
متن کاملCorrosion Resistance Enhancement of AZ91 Magnesium Alloy Using Ni-P Interlayer and Electrophoretic Deposited 3YSZ Coating
The zirconia stabilized by 3mol % Y2O3 (3YSZ) was applied onto the surface of the magnesium alloy AZ91D using electrophoretic deposition (EPD) from a non- aqueous solution. A Ni-P interlayer between the substrate and YSZ coating was also prepared by electroless plating. Finally, coatings were heat treated in control atmosphere at 400 °C. The preparation, microstructure and corrosion resistance ...
متن کاملBiocompatibility and Corrosion Protection Behaviour of Hydroxyapatite Sol-Gel-Derived Coatings on Ti6Al4V Alloy
The aim of this work was to prepare hydroxyapatite coatings (HAp) by a sol-gel method on Ti6Al4V alloy and to study the bioactivity, biocompatibility and corrosion protection behaviour of these coatings in presence of simulated body fluids (SBFs). Thermogravimetric/Differential Thermal Analyses (TG/DTA) and X-ray Diffraction (XRD) have been applied to obtain information about the phase transfor...
متن کاملCharacterization of hydroxyapatite containing micro-arc oxidation coating on ZK60 magnesium alloy
INTRODUCTION: Magnesium alloys are attractive as a class of biodegradable metallic materials. However, too fast degradation is an obstacle to their clinical applications. Recently, micro-arc oxidation (MAO) coatings were applied on biodegradable magnesium alloys to delay their degradation. In vivo studies showed that the protective ability of the MAO coating should be further improved [1]. Seal...
متن کاملOxide Film and Porosity Defects in Magnesium Alloy Az91
Porosity is a major concern in the production of light metal parts. This work aims to identify some of the mechanisms of microporosity formation in magnesium alloy AZ91. Microstructure analysis was performed on several samples obtained from gravity-poured ingots in graphite plate molds. Temperature data during cooling was acquired with type K thermocouples at 60 Hz at three locations of each ca...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Pamukkale University Journal of Engineering Sciences
سال: 2017
ISSN: 1300-7009,2147-5881
DOI: 10.5505/pajes.2017.34270