Hydrophobic, mechanical and thermal characteristics of thermoplastic cellulose diacetate bonded with cardanol from cashew nutshell
نویسندگان
چکیده
منابع مشابه
Mechanical, Morphological, and Thermal Properties of Nutshell and Microcrystalline Cellulose Filled High- Density Polyethylene Composites
Effects of nutshell fiber loadings of 30 wt.% and MCC loadings up to 15 wt.% on some properties of high-density polyethylene composites (HDPE) were investigated. The composites were manufactured by a single screw extruder and injection molding. The experimental composite samples were tested for their mechanical performance including tensile strength, tensile modulus, flexural strength, flexural...
متن کاملThermal and Magnetic Characteristics of Cellulose Acetate- Fe3O4
Fe3O4 nanoparticles were synthesizedviaa simple chemical reaction between FeCl2.4H2O and Fe(NO3)3.9H2O under nitrogen atmosphere at room temperature, and then nanoparticles were added to cellulose acetate (CA) polymer. The influence of nanoparticles on the thermal properties of CA polymeric matrix was studied using the...
متن کاملNanoindentation of Biodegradable Cellulose Diacetate-graft-Poly(L-lactide) Copolymers: Effect of Molecular Composition and Thermal Aging on Mechanical Properties
Nanoindentation of cellulose diacetate-graft-poly(lactide)s (CDA-g-PLLAs) synthesized by ring opening graft copolymerization of L-lactide in bulk onto the residual hydroxyl positions on CDA were conducted to investigate the effect of the molecular composition and thermal aging on mechanical properties and creep behavior. Continuous stiffness measurement (CSM) technique was used to obtained hard...
متن کاملimprovement in mechanical properties of cellulose fibers-thermoplastic polymer composites
0
متن کاملThermal and Dynamic Mechanical Properties of Hydroxypropyl Cellulose Films
DifI'..tial scanning calorimetry (~ and dynamic ~-,!jCaJ thermal analysis (DMTA) were used to characterize the morphology of eolv81t cast hydroXYPl'Opyl ceUuloee (Hpc) films. DSC r-.lta windicative of a aemicryltaUine mat«ial with a melt at 220°C and a ,tran8itioo at 19°C (T1). althoucb an 8dditiCXlal _t wu MIumted by a baseline inftectioo at about ~C (Tt). Cc pcx1din, relaxatiMS wfound by DMTA...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Polymer Journal
سال: 2011
ISSN: 0032-3896,1349-0540
DOI: 10.1038/pj.2011.57