Hydrogen Sorption Behaviors of a Core–Shell Structured Mg@Fe Composite Powder
نویسندگان
چکیده
منابع مشابه
Hydrogen sorption properties of a MgH2 - V2O5 composite prepared
A 90 wt.% MgH2 – 10 wt.% V2O5 composite was obtained by ball milling of a mixture of magnesium hydride and vanadia for 60 min under argon. Hydrogen sorption properties of the composite were determined volumetrically with a Sieverts-type device. Absorption was studied at temperatures of 473 and 573 K and pressure of 1 MPa, while desorption was investigated at T = 573 and 623 K and P = 0.15 MPa. ...
متن کاملA Novel Self-Assembling Al-based Composite Powder with High Hydrogen Generation Efficiency
In this study, a novel self-assembling hydrogen generation powder comprised of 80Al-10Bi-10Sn wt.% was prepared using the gas atomization method and then collected in an air environment. The morphological and hydrolysis properties of the powders were investigated. The results indicated that the powders formed unique core/shell microstructures with cracked surfaces and (Bi, Sn)-rich phases distr...
متن کاملElectrochemical Synthesis of Core–Shell-Structured NbC–Fe Composite Powder for Enforcement in Low-Carbon Steel
An NbC-Fe composite powder was synthesized from an Nb₂O₅/Fe/C mixture by electrochemical reduction and subsequent carbonization in molten CaCl₂-NaCl. The composite has a core-shell structure, in which NbC acts as the cores distributing in the Fe matrix. A strong bonding between NbC and Fe is benefit from the core-shell structure. The sintering and electrochemical reduction processes were invest...
متن کاملPositron Spectroscopy of Nanodiamonds after Hydrogen Sorption
The structure and defects of nanodiamonds influence the hydrogen sorption capacity. Positronium can be used as a sensor for detecting places with the most efficient capture of hydrogen atoms. Hydrogenation of carbon materials was performed from gas atmosphere. The concentration of hydrogen absorbed by the sample depends on the temperature and pressure. The concentration 1.2 wt % is achieved at ...
متن کاملHydrogen sorption in functionalized metal-organic frameworks.
Five porous metal-organic frameworks based on linking zinc oxide clusters with benzene-1,4-dicarboxylate, naphthalene-2,6-dicarboxylate, 4,5,9,10-tetrahydropyrene-2,7-dicarboxylate, 2,3,5,6-tetramethylbenzene-1,4-dicarboxylate, or benzene-1,3,5-tris(4-benzoate) were synthesized in gram-scale quantities to measure their hydrogen uptake properties. Hydrogen adsorption isotherms measured at 77 K s...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2014
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.mg201418