Hydrogen Embrittlement Properties of Ultra High-strength Low Alloy TRIP-aided Steels with Bainitic Ferrite Matrix
نویسندگان
چکیده
منابع مشابه
High-Strength Bainitic Steels
With careful design, mixed microstructures consisting of fine plates of upper bainitic ferrite separated by thin films of stable retained austenite have exhibited impressive combinations of strength and toughness in highsilicon bainitic steels. The silicon suppresses the precipitation of brittle cementite leading to an improvement in toughness. The essential principles governing the optimisatio...
متن کاملULTRA FINE FERRITE FORMATION IN Si-Mn TRIP STEELS
Abstract: In the present investigation, the effects of thermomechanical processing parameters and the steel chemical composition on the ultra fine ferrite formation characteristics were studied. This was programmed relying on the capabilities of strain induced transformation (SIT) phenomenon and applying to different grades of Si-Mn TRIP (Transformation Induced Plasticity) steels. According...
متن کاملCharacteristics of Hydrogen Embrittlement, Stress Corrosion Cracking and Tempered Martensite Embrittlement in High-strength Steels
Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...
متن کاملhigh-strength bainitic steels
with careful design, mixed microstructures consisting of fine plates of upper bainitic ferrite separated by thinfilms of stable retained austenite have exhibited impressive combinations of strength and toughness in highsiliconbainitic steels. the silicon suppresses the precipitation of brittle cementite leading to an improvement intoughness. the essential principles governing the optimisation o...
متن کاملEstimation of Atmospheric Corrosion of High-Strength, Low-Alloy Steels
This data analysis was undertaken to investigate the weatherability of steels whose compositions do not fall in the range of ASTM Standard G101, Estimating the Atmospheric Corrosion Resistance of Low-Alloy Steels (1). This standard was developed to estimate the corrosion resistance of low-alloy weathering steels from chemical composition data and from actual atmospheric exposure tests. This sta...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 2006
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.92.2_83