Hydrogen Embrittlement of Steels under Constant Load Rupture Test (Report 3)
نویسندگان
چکیده
منابع مشابه
Prevention of Hydrogen Embrittlement in Steels
The essential facts about the nature of the hydrogen embrittlement of steels have now been known for 140 years. It is diffusible hydrogen that is harmful to the toughness of iron. It follows, therefore, that the harmful influence of diffusible hydrogen can be mitigated by preventing its entry into steel or by rendering it immobile once it penetrates the material. This review deals with the meth...
متن کاملCharacteristics of Hydrogen Embrittlement, Stress Corrosion Cracking and Tempered Martensite Embrittlement in High-strength Steels
Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...
متن کاملEffects of tungsten on the hydrogen embrittlement behaviour of microalloyed steels
The effects of tungsten (W) additions (0, 0.1, 0.5 and 1 wt.%) on the hydrogen embrittlement behaviour of microalloyed steels were systematically investigated by means of slow strain rate tests on circumferentially notched cylindrical specimens, and the mechanism of hydrogen-induced embrittlement was discussed. W addition is found to increase the activation energy of hydrogen desorption. Micros...
متن کاملStudy on Temper Embrittlement and Hydrogen Embrittlement of a Hydrogenation Reactor by Small Punch Test
The study on temper embrittlement and hydrogen embrittlement of a test block from a 3Cr1Mo1/4V hydrogenation reactor after ten years of service was carried out by small punch test (SPT) at different temperatures. The SPT fracture energy Esp (derived from integrating the load-displacement curve) divided by the maximum load (Fm) of SPT was used to fit the Esp/Fm versus-temperature curve to determ...
متن کاملA Comparison of Hydrogen Embrittlement and Stress Corrosion Cracking in High Strength Steels
The purpose of this study was to compare the known behavior of hydrogen embrittled high-strength steel to the characteristics of environmentallyinduced stress corrosion failure where hydrogen is continuously generated at the specimen surface. The incubation time for the initiation of slow crack growth was accelerated by prestressing for a fixed time below the lower critical limit. These results...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Welding Society
سال: 1967
ISSN: 0021-4787,1883-7204
DOI: 10.2207/qjjws1943.36.1024