Hydrogen Embrittlement of Sensitized Inconel 600.
نویسندگان
چکیده
منابع مشابه
Prevention of Hydrogen Embrittlement in Steels
The essential facts about the nature of the hydrogen embrittlement of steels have now been known for 140 years. It is diffusible hydrogen that is harmful to the toughness of iron. It follows, therefore, that the harmful influence of diffusible hydrogen can be mitigated by preventing its entry into steel or by rendering it immobile once it penetrates the material. This review deals with the meth...
متن کاملCharacteristics of Hydrogen Embrittlement, Stress Corrosion Cracking and Tempered Martensite Embrittlement in High-strength Steels
Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...
متن کاملStudy on Temper Embrittlement and Hydrogen Embrittlement of a Hydrogenation Reactor by Small Punch Test
The study on temper embrittlement and hydrogen embrittlement of a test block from a 3Cr1Mo1/4V hydrogenation reactor after ten years of service was carried out by small punch test (SPT) at different temperatures. The SPT fracture energy Esp (derived from integrating the load-displacement curve) divided by the maximum load (Fm) of SPT was used to fit the Esp/Fm versus-temperature curve to determ...
متن کاملOn the microstrctral and machanical properties of similar TLP bonding of Inconel 600 superalloy sheet
In this study, microstructural evaluation and mechanical properties of similar TLP bonded of Inconel 600 by using of BNi-2 interlayer were investigated. The bonding tests were carried out at 1050°C and 1100°C for 5-45 min which homogenization treatment was performed on the best of the bonded samples. Results showed that Ni-B eutectic compound was formed in the a-thermally solidification zone (A...
متن کاملThe Effect of Al2O3-MWCNT Hybrid Nanofluid on Surface Quality in Grinding of Inconel 600
Grinding is finishing process aimed at achieving surface quality and dimensional accuracy in workpieces with tight tolerances especially from materials with a high degree of hardness and strength. The grinding process of superalloys is faced with problems and challenges caused by the generation of excessiveheatas well as the adhesion of workpiecematerialon the grinding tool. Therefore, in-depth...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1997
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.46.526