Hydrogen Embrittlement of Cold-Worked SUS304 Steel Single Crystal.

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Relaxation Peaks of Cold Worked 304l Stainless Steel

In this investigation internal friction of cold worked 304L austenitic stainless steel was measured and the new peaks (PlIP2,P3) were found. The height of those peaks increased with cold work degree. The temperature of the main peak P3 was 33513340K at the frequency of -1,000Hz. The activation energies and frequency factors were obtained from peak shift. The values were 0.4evl 0.4evl 0.6ev and ...

متن کامل

Hydrogen Embrittlement Behavior of a 1700 MPa-Class Ultrahigh Strength Steel Containing Hydrogen Traps

Eiji Akiyama , Songjie Li , Yuuji Kimura , Kaneaki Tsuzaki , Nobuyoshi Uno c a National Institute for Materials Science 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan b School of Materials Science and Engineering, University of Science and Technology Beijing, No. 30 Xueyuan Road, Hidian Zone, Beijing 100083, China c Nippon Steel and Sumikin Metal Products Co, Ltd, SA Bldg., 17-12 Kiba 2-chome, ...

متن کامل

Hydrogen Embrittlement of Duplex Steel Tested Using Slow Strain Rate Test

P. Vaňová, J. Sojka. VŠB Technical u niversity of O strava, FMME, Ostrava, Czech Republic This paper is dealing with hydrogen embrittlement of austenitic-ferritic 2205 duplex steel using the slow strain rate test (SSRT). The original material was subjec ted to heat treatment under 700 °C during 5 hours and f ollowing aircooling with the aim of pr ovoking sigma phase pr ecipitation and embrittle...

متن کامل

Hydrogen Embrittlement of High Strength Steel Electroplated with Zinc-cobalt Alloys

Slow strain rate tests were performed on quenched and tempered AISI 4340 steel to measure the extent of hydrogen embrittlement caused by electroplating with zinc-cobalt alloys. The effects of bath composition and pH were studied and compared with results for electrodeposited cadmium and zinc-10%nickel. It was found that Zinc-1%cobalt alloy coatings caused serious hydrogen embrittlement (EI 0.63...

متن کامل

Warm Pre-Strain: Strengthening the Metastable 304L Austenitic Stainless Steel without Compromising Its Hydrogen Embrittlement Resistance

Plastic pre-strains were applied to the metastable 304L austenitic stainless steel at both room temperature (20 °C) and higher temperatures (i.e., 50, 80 and 100 °C), and then the hydrogen embrittlement (HE) susceptibility of the steel was evaluated by cathodically hydrogen-charging and tensile testing. The 20 °C pre-strain greatly strengthened the steel, but simultaneously significantly increa...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Journal of the Society of Materials Science, Japan

سال: 1995

ISSN: 1880-7488,0514-5163

DOI: 10.2472/jsms.44.1423