Hydrogen embrittlement in a 2101 lean Duplex Stainless Steel
نویسندگان
چکیده
منابع مشابه
Warm Pre-Strain: Strengthening the Metastable 304L Austenitic Stainless Steel without Compromising Its Hydrogen Embrittlement Resistance
Plastic pre-strains were applied to the metastable 304L austenitic stainless steel at both room temperature (20 °C) and higher temperatures (i.e., 50, 80 and 100 °C), and then the hydrogen embrittlement (HE) susceptibility of the steel was evaluated by cathodically hydrogen-charging and tensile testing. The 20 °C pre-strain greatly strengthened the steel, but simultaneously significantly increa...
متن کاملHydrogen Embrittlement of Duplex Steel Tested Using Slow Strain Rate Test
P. Vaňová, J. Sojka. VŠB Technical u niversity of O strava, FMME, Ostrava, Czech Republic This paper is dealing with hydrogen embrittlement of austenitic-ferritic 2205 duplex steel using the slow strain rate test (SSRT). The original material was subjec ted to heat treatment under 700 °C during 5 hours and f ollowing aircooling with the aim of pr ovoking sigma phase pr ecipitation and embrittle...
متن کاملKinetics of Sigma Phase Formation In a Duplex Stainless Steel
This work determines the kinetics of sigma phase formation in UNS S31803 Duplex Stainless Steel (DSS), describing the phase transformations that occur in isothermal aging between 700 and 900 °C for time periods up to 1032 hours, allowing the determination of the Time-Temperature-Precipitation (TTP) diagram for sigma phase and proposing a model to predict the kinetics of sigma phase formation us...
متن کاملStudy on Static Recrystallization Process in Duplex Stainless Steel 2205
Steel 2205 is one of the most famous duplex stainless steels. The microstructure of this steel composed of ferrite and austenite in similar amount. Therefore, in order to improve mechanical properties through microstructure, thermo mechanical processes such as controlled hot rolling and forging should be applied. It is not possible to employ the usual heat treatment. It shows the importance of ...
متن کاملCrystallography of Widmanstätten austenite in duplex stainless steel weld metal
Two kinds of austenite grow from d-ferrite during the cooling of the duplex stainless steel weld deposits studied here, Widmanstätten plates and allotriomorphs which precipitate at d–d grain boundaries. It is found using microtexture measurements that the preferred crystallographic orientation of the Widmanstätten austenite can be estimated using established theory if it is assumed that there i...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Structural Integrity
سال: 2019
ISSN: 2452-3216
DOI: 10.1016/j.prostr.2019.08.180