Hydrogen Embrittlement for High Strength Steel Treated with Zinc and Zinc-Nickel Alloy Electroplating from a Sulfate Bath and Hydrogen Permeability
نویسندگان
چکیده
منابع مشابه
Hydrogen Embrittlement of High Strength Steel Electroplated with Zinc-cobalt Alloys
Slow strain rate tests were performed on quenched and tempered AISI 4340 steel to measure the extent of hydrogen embrittlement caused by electroplating with zinc-cobalt alloys. The effects of bath composition and pH were studied and compared with results for electrodeposited cadmium and zinc-10%nickel. It was found that Zinc-1%cobalt alloy coatings caused serious hydrogen embrittlement (EI 0.63...
متن کاملHydrogen Embrittlement Behavior of a 1700 MPa-Class Ultrahigh Strength Steel Containing Hydrogen Traps
Eiji Akiyama , Songjie Li , Yuuji Kimura , Kaneaki Tsuzaki , Nobuyoshi Uno c a National Institute for Materials Science 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan b School of Materials Science and Engineering, University of Science and Technology Beijing, No. 30 Xueyuan Road, Hidian Zone, Beijing 100083, China c Nippon Steel and Sumikin Metal Products Co, Ltd, SA Bldg., 17-12 Kiba 2-chome, ...
متن کاملCharacteristics of Hydrogen Embrittlement, Stress Corrosion Cracking and Tempered Martensite Embrittlement in High-strength Steels
Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...
متن کاملPitting-induced hydrogen embrittlement of magnesium- aluminium alloy
In this study, the pitting corrosion susceptibility and its role on the hydrogen embrittlement behavior of AZ80 magnesium alloy were studied using slow strain rate testing (SSRT), electrochemical technique and immersion test method. The electrochemical and immersion tests in chloride-containing solution revealed severe pitting corrosion in the alloy. The SSRT results of the alloy under continuo...
متن کاملHydrogen embrittlement of grain boundaries in nickel: an atomistic study
The chemomechanical degradation of metals by hydrogen is widely observed, but not clearly understood at the atomic scale. Here we report an atomistic study of hydrogen embrittlement of grain boundaries in nickel. All the possible interstitial hydrogen sites at a given grain boundary are identified by a powerful geometrical approach of division of grain boundary via polyhedral packing units of a...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of The Surface Finishing Society of Japan
سال: 2019
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.70.110