Hot Pressing Consolidation Mechanisms of Bulk Metallic Glass Powders
نویسندگان
چکیده
منابع مشابه
Mg–Y–Cu bulk metallic glass prepared by mechanical alloying and vacuum hot-pressing
We have studied the amorphization behavior of Mg85KxY15Cux (xZ20–40) alloy powders synthesized by mechanical alloying technique. The as-milled powders were mainly amorphous after 10 h of milling. The thermal stability of these Mg85KxY15Cux glassy powders was investigated by differential scanning calorimeter (DSC). The ranges of Tg, Tx and DTx are around 430–459, 467–497, and 30–46 K, respective...
متن کاملHot embossing of micro-lens array on bulk metallic glass
Hot embossing of micro-lens array on bulk metallic glass C.T. Pan a,∗, T.T. Wu a, M.F. Chen a, Y.C. Chang b, C.J. Lee b, J.C. Huang b a Department of Mechanical and Electro-Mechanical Engineering, and Center for Nanoscience & Nanotechnology, National Sun Yat-Sen University, Kaoshiung 804, Taiwan, ROC b Institute of Materials Science & Engineering, Center for Nanoscience and Nanotechnology, Nati...
متن کاملDuctile bulk metallic glass.
We report on experimental evidence of pronounced global plasticity measured in monolithic Pt57.5Cu14.7Ni5.3P22.5 bulk metallic glass under both bending and unconfined compression loading conditions. A plastic strain of 20% is measured, never before seen in metallic glasses. Also, permanent deformation and a strain exceeding 3% before failure is observed during bending of 4 mm thick samples. To ...
متن کاملDeformation Mechanisms of Bulk Metallic Glass Matrix Composites
Bulk metallic glasses (BMGs) possess a unique set of mechanical properties that make them attractive structural materials: yield strength > 2 GPa, fracture toughness ~20 MPa.m and elastic strain limit ~2%. BMGs can also be cast into intricate shapes which retain their dimensional integrity and require no further machining. Unfortunately, monolithic BMGs fail catastrophically under unconstrained...
متن کاملArgon-shielded hot pressing of titanium alloy (Ti6Al4V) powders.
The paper presents the method of the argon - shielded hot pressing of titanium alloy (Ti6A14V) powder (used in medical industry). The powders produced in the GA (gas atomization) process and in the HDH (hydride - dehydride) process were used in the experiments. A pressing process was conducted at a temperature of 800-850 degrees C for different lengths of time. An unoxidized sintered material, ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 2007
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.54.761