Hot Ductility Test of Austenitic Stainless Steel Weld Metals
نویسندگان
چکیده
منابع مشابه
An evaluation of weld metal nitrogen retention and properties in 316LN austenitic stainless steel
A series of tests were conducted using varying levels of nitrogen and helium in a conventional argon shielding gas when welding 316LN austenitic stainless steel. The outcome was that a 15 per cent nitrogen addition to the argon shielding gas had the most significant effect on increasing the weld metal nitrogen. Subsequent additions of helium to the argon 15 per cent nitrogen shielding gas had v...
متن کاملOptimization of Weld Bead Width in Tungsten Inert Gas Welding of Austenitic Stainless Steel Alloy
This paper investigates the effects of process parameters on weld bead width of austenitic stainless steel SS-310 in tungsten inert gas welding. The four parameters namely welding current, type of gas, gas flow rate and included angle of weld plates during butt joint were varied at three levels. The DOE approach was used to design experimental conditions. Orthogonal array L9 was used for carryi...
متن کاملThe adhesion of hot-filament CVD diamond films on AISI type 316 austenitic stainless steel
Steel ball indentation and scratch adhesion testing of hot filament chemical vapour deposited diamond films onto AISI type 316 austenitic stainless steel substrates using two different interlayer systems, namely chromium nitride and borided steel, have been investigated. In order to compare the adhesion of these films with that of a well-known and strongly adherent system, detailed adhesion tes...
متن کاملGrain Size Effect on the Hot Deformation Processing Map of AISI 304 Austenitic Stainless Steel
In this study, the hot deformation processing map of AISI 304 austenitic stainless steel in two initial grain sizes of 15 and 40 μm was investigated. For this purpose, cylindrical samples were used in the hot compression test at the temperature range of 950-1100 °C and the strain rate of 0.005-0.5% s-1. At first, the relationship between the peak stress and Zener-Hollomon parameter w...
متن کاملSensitization Behavior of Gnaw Austenitic Stainless Steel Joints
The present work has been carried out to study the sensitization behavior of AISI 304L austenitic stainless steel weld, fabricated using GTAW (gas tungsten arc welding process). This weld was subjected to post weld thermal aging (PWTA) treatments lying in the sensitization range, viz. 700 ?C for 30 minutes, 500 minutes and 1000 minutes for studying the influence of carbide precipitation on thei...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Welding Society
سال: 1960
ISSN: 0021-4787,1883-7204
DOI: 10.2207/qjjws1943.29.30