Hot Deformation of Austenite in a Plain Carbon Steel
نویسندگان
چکیده
منابع مشابه
Dynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملNeural Network Modelling of Hot Deformation of Austenite Conference Item
The hot deformation behaviour of austenite in steels is a complicated process which depends on chemical composition, microstructure, temperature and strain rate. While many models have been developed to represent the flow stress as a function of these variables, it is not yet possible to predict the behaviour for a new alloy. Linear regression techniques are not capable of representing the data...
متن کاملNeural network modelling of hot deformation of austenite
The hot deformation behaviour of austenite in steels is a complicated process which depends on chemical composition, microstructure, temperature and strain rate. While many models have been developed to represent the flow stress as a function of these variables, it is not yet possible to predict the behaviour for a new alloy. Linear regression techniques are not capable of representing the data...
متن کاملThe Effect of Hot Deformation Parameters on Grain Size Refinement in a Martensitic Stainless Steel
The grain size refinement of AISI 422 martensitic stainless steel in the temperature range of 950-1150 ºC was investigated by hot deformation tests. The deformed specimens were held at deformation temperature with delay times of 5 to 300s after achieving a strain of 0.3. The austenite grains exhibit a considerable growth at temperature higher than 1050˚C, while the grain coarsening is negligibl...
متن کاملdynamic recrystallization under hot deformation of a ph stainless steel
dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Iron and Steel Institute of Japan
سال: 1977
ISSN: 0021-1583,1881-1183
DOI: 10.2355/isijinternational1966.17.718