Hot Deformation Behavior of Ti-3.5Al-5Mo-6V-3Cr-2Sn-0.5Fe Alloy in α + β Field
نویسندگان
چکیده
منابع مشابه
Hot Deformation Behavior of Ti-3.5Al-5Mo-6V-3Cr-2Sn-0.5Fe Alloy in α + β Field
The deformation behavior of Ti-3.5Al-5Mo-6V-3Cr-2Sn-0.5Fe high strength β titanium alloy is systematically investigated by isothermal compression in α + β field with the deformation temperatures ranging from 1003 K to 1078 K, the strain rates ranging from 0.001 s to 1 s and the height reduction is around 50%. Essentially, the flow stress-strain curve of isothermal compression in α + β field exh...
متن کاملFlow Behavior of SP-700 Titanium Alloy During Hot Tensile Deformation in α+β and β Phase Regions
In this paper, in order to study the flow behavior and elongation of as-cast ingots of SP-700 titanium alloy, hot tensile test was done in α/β dual phase and β single phase regions using strain rate of 0.1 s-1. Results showed that the hot tensile behavior of SP-700 in the α/β dual phase region (700-900 ºC) was different from the β single phase one (950-1100 ºC) due to the nature of alpha and be...
متن کاملMicrostructural Evaluation of Ti-6AL-4V Alloy during Hot Deformation
Among the titanium alloys, Ti-6Al-4V is the most widely used. In the present work, the uniaxial hot compressive behavior of Ti-6Al-4V has been investigated under constant strain rates. A series of dilatometery experiments were carried out to determine the transformation temperatures at different cooling rates. Specimens were homogenized at 1050 °C for 10 minutes followed by fast cooling to dif...
متن کاملMicrostructural Evaluation of Ti-6AL-4V Alloy during Hot Deformation
Among the titanium alloys, Ti-6Al-4V is the most widely used. In the present work, the uniaxial hot compressive behavior of Ti-6Al-4V has been investigated under constant strain rates. A series of dilatometery experiments were carried out to determine the transformation temperatures at different cooling rates. Specimens were homogenized at 1050 °C for 10 minutes followed by fast cooling to dif...
متن کاملPseudo-elastic deformation behavior in a Ti/Mo-based alloy
It is shown that the pseudo-elastic response in a series of Ti–Mo–V–Nb–Al alloys with 8–11 wt.% Mo is highly sensitive to both composition and heat treatment. Recovery of up to 3.0% strain has been observed but it appears that this may not be due to reversible formation of a00 martensite. 2003 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.