Hot Deformation Behavior of a New Nuclear Use Reduced Activation Ferritic/Martensitic Steel
نویسندگان
چکیده
منابع مشابه
Hot Deformation Behavior of 17-7 PH Stainless Steel
To investigate the hot deformation behavior of 17-7 PH stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oC and strain rates of 0.001 s-1 to 0.1 s-1. Accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. ...
متن کاملEVALUATING HOT DEFORMATION BEHAVIOR OF W360 TOOL STEEL BY HOT COMPRESSION TEST
In this research, the hot deformation behavior of W360 tool steel was investigated using hot compression test at 1000-1200°C and strain rates of 0.001, 0.01, 0.1, and 1 s-1. According to the results, dynamic recrystallization was found the most important restoration factor of this alloy during hot deformation. Recrystallization was enhanced with an increase in temperature and strain rate. Also,...
متن کاملHot tensile properties of 9Cr-2WVTa reduced-activation ferritic/martensitic steel
Reduced-activation ferritic/martensitic steels have been developed by replacing molybdenum by tungsten and niobium by tantalum in commercial elevated-temperature Cr–Mo steels to reduce half-life of radioactive isotopes. The objective of this study was to investigate tensile properties of a reduced-activation ferritic/martensitic steel (9Cr-2WVTa) in normalized-tempered (NT) and quenched-tempere...
متن کاملhot deformation behavior of 17-7 ph stainless steel
to investigate the hot deformation behavior of 17-7 ph stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oc and strain rates of 0.001 s-1 to 0.1 s-1. accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. ...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Metallurgica Sinica (English Letters)
سال: 2018
ISSN: 1006-7191,2194-1289
DOI: 10.1007/s40195-018-0851-0