Hot Deformation Behavior and Processing Map of a Cu-Bearing 2205 Duplex Stainless Steel
نویسندگان
چکیده
منابع مشابه
Grain Size Effect on the Hot Deformation Processing Map of AISI 304 Austenitic Stainless Steel
In this study, the hot deformation processing map of AISI 304 austenitic stainless steel in two initial grain sizes of 15 and 40 μm was investigated. For this purpose, cylindrical samples were used in the hot compression test at the temperature range of 950-1100 °C and the strain rate of 0.005-0.5% s-1. At first, the relationship between the peak stress and Zener-Hollomon parameter w...
متن کاملHot Deformation Behavior of 17-7 PH Stainless Steel
To investigate the hot deformation behavior of 17-7 PH stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oC and strain rates of 0.001 s-1 to 0.1 s-1. Accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. ...
متن کاملMicrostructural refining during friction stir processing of SAF 2205 duplex stainless steel
Friction stir processing (FSP) was conducted on a SAF 2205 duplex stainless steel at advancing speed of 50 mm/min and rotational speed of 400 rpm. Characterization of evolved material was studied using electron microscopy equipped with electron back scattered diffraction (EBSD) system. The results indicated that the severe plastic deformation and the heat generated during the FSP developed a v...
متن کاملStudy on Static Recrystallization Process in Duplex Stainless Steel 2205
Steel 2205 is one of the most famous duplex stainless steels. The microstructure of this steel composed of ferrite and austenite in similar amount. Therefore, in order to improve mechanical properties through microstructure, thermo mechanical processes such as controlled hot rolling and forging should be applied. It is not possible to employ the usual heat treatment. It shows the importance of ...
متن کاملhot deformation behavior of 17-7 ph stainless steel
to investigate the hot deformation behavior of 17-7 ph stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oc and strain rates of 0.001 s-1 to 0.1 s-1. accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Metallurgica Sinica (English Letters)
سال: 2019
ISSN: 1006-7191,2194-1289
DOI: 10.1007/s40195-019-00910-6