Hot Deformation and Dynamic Recrystallization Behavior of CoCrNi and (CoCrNi)94Ti3Al3 Medium Entropy Alloys

Dynamic Recrystallization under Hot Deformation of a PH Stainless Steel

Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...

In situ study of dynamic recrystallization and hot deformation behavior of a multiphase titanium aluminide alloy

multiphase titanium aluminide alloy Klaus-Dieter Liss, Thomas Schmoelzer, Kun Yan, Mark Reid, Matthew Peel, Rian Dippenaar, and Helmut Clemens Australian Nuclear Science and Technology Organisation, PMB 1, Menai, New South Wales 2234, Australia Department of Physical Metallurgy and Materials Testing, Montanuniversität, A-8700 Leoben, Austria Faculty of Engineering, University of Wollongong, Wol...

dynamic recrystallization under hot deformation of a ph stainless steel

dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...

Deformation and Recrystallization Behaviors in Magnesium Alloys

Deformation Behavior of Al0.25CoCrFeNi High-Entropy Alloy after Recrystallization

Cold rolling with subsequent annealing can be used to produce the recrystallized structure in high entropy alloys (HEAs). The Al0.25CoCrFeNi HEAs rolled to different final thickness (230, 400, 540, 800, 1000, 1500 μm) are prepared to investigate their microstructure evolutions and mechanical behaviors after annealing. Only the single face-centered cubic phase was obtained after cold rolling and...