Highly Efficient Elimination of Carbon Monoxide with Binary Copper-Manganese Oxide Contained Ordered Nanoporous Silicas
نویسندگان
چکیده
منابع مشابه
Highly Efficient Elimination of Carbon Monoxide with Binary Copper-Manganese Oxide Contained Ordered Nanoporous Silicas
Ordered nanoporous silicas containing various binary copper-manganese oxides were prepared as catalytic systems for effective carbon monoxide elimination. The carbon monoxide elimination efficiency was demonstrated as a function of the [Mn]/[Cu] ratio and reaction time. The prepared catalysts were characterized by Brunauer-Emmett-Teller (BET) method, small- and wide-angle X-ray diffraction (XRD...
متن کاملCobalt promoted copper manganese oxide catalysts for ambient temperature carbon monoxide oxidation.
Low levels of cobalt doping (1 wt%) of copper manganese oxide enhances its activity for carbon monoxide oxidation under ambient conditions and the doped catalyst can display higher activity than current commercial catalysts.
متن کاملStudy of Nitric Oxide (no) Reduction with Carbon Monoxide 1 (co) as Reducing Agent over Copper Oxide Supported on 2 Mesoporous Alumina and Manganese Oxide 3
12 The activities of copper oxide supported on mesoporous alumina and manganese oxide 13 have been investigated for nitric oxide (NO) reduction using carbon monoxide (CO) as 14 reducing agent. The results showed that catalytic activity is strongly influenced by the 15 properties of supports. CuO supported on manganese oxide was found to be a more 16 active catalyst for the NO reduction as compa...
متن کاملcatalytic oxidation of carbon monoxide using copper-zinc mixed oxide nanoparticles supported on diatomite
background diatomite coated by nanoparticles of copper and zinc mixed oxides were used to investigate catalytic oxidation of carbon monoxide. objectives aim of this paper was to investigatediatomite performance as a supporting host to confine the cuo and zno nanoparticles and its catalytic activity for carbon monoxide oxidation. materials and methods the prepared catalysts were characterized by...
متن کاملCatalytically active ceria-supported cobalt-manganese oxide nanocatalysts for oxidation of carbon monoxide.
A low-concentration cobalt (∼6 at%) and manganese (∼3 at%) bimetallic oxide catalyst supported on ceria nanorods (CoMnOx/CeO2), as well as its related single metal oxide counterparts (CoOx/CeO2 and MnOx/CeO2) was synthesized via a deposition-precipitation approach. The fresh samples after air-calcination at 400 °C were tested under the reaction conditions of CO oxidation, and showed the followi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanoscale Research Letters
سال: 2016
ISSN: 1931-7573,1556-276X
DOI: 10.1186/s11671-015-1197-4