FePt magnetic thin films (20 nm) were deposited on SrTiO3 (1 0 0) single-crystal substrates at 150, 250, and 350 1C by DC magnetron sputtering. The dependence of the structural and magnetic properties of the FePt films on the substrate temperature was studied. At 150 1C, the FePt film showed a (1 1 1) preferred orientation. At 250 1C, the superlattice FePt (0 0 1) peak appeared indicating that ...

Effect of lattice mismatch on chemical ordering of epitaxial L10 FePt films

The effect of lattice mismatch on the chemical ordering of epitaxial FePt films was studied. The results showed that the lattice constant scd of the FePt films decreased with increasing lattice mismatch « from about 2.23% to 6.33%. Upon further increase of « to about 8.8%, c increased. On the other hand, the variation of the lattice constant sad of the FePt films showed a reversal behavior to t...