High temperature workability behaviour of a modified P92 steel
نویسندگان
چکیده
منابع مشابه
Corrosion Behaviour of Nickel Coated AISI 316 Stainless Steel as a Function of Annealing Temperature
AISI 316 stainless steels were coated with 250 nm Ni film by electron beam deposition and post-annealed at different temperatures with a nitrogen flow of 600 cm3min-1 nitrogen. The prepared samples were corrosion tested in 1.0 M sulphuric acid solution using potentiodynamic technique. Crystallographic and morphological structure of the samples were analyzedanalysed by X-ray diffraction (XRD) an...
متن کاملPREDICTION OF HOT DEFORMATION BEHAVIOUR OF A PH STAINLESS STEEL AT HIGH STRAIN RATES
In this study the hot deformation behaviour of a precipitation hardened (PH) stainless steel at high strain rates has been predicted through hot compression testing. Stress-strain curves were obtained for a range of strain rates from 10-3 to 10+1 S-1 and temperatures from 850 to 1150°C. Results obtained by microstructure and stress-strain curves show that at low temperatures and high strain rat...
متن کاملDynamic Recrystallization and Hot Workability of 316LN Stainless Steel
Chaoyang Sun 1,*, Yu Xiang 1, Qingjun Zhou 2, Denis J. Politis 3, Zhihui Sun 1,* and Mengqi Wang 1 1 School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China; [email protected] (Y.X.); [email protected] (M.W.) 2 Capital Aerospace Machinery Company, Beijing 100076, China; [email protected] 3 Department of Mechanical Engineering, Imperial Co...
متن کاملA Fine Grain, High Mn Steel with Excellent Cryogenic Temperature Properties and Corresponding Constitutive Behaviour
A Fe-34.5 wt % Mn-0.04 wt % C ultra-high Mn steel with a fully recrystallised fine-grained structure was produced by cold rolling and subsequent annealing. The steel exhibited excellent cryogenic temperature properties with enhanced work hardening rate, high tensile strength, and high uniform elongation. In order to capture the unique mechanical behaviour, a constitutive model within finite str...
متن کاملMagnetic Evaluation of Water-Quenched Modified 9Cr1Mo Steel Subjected to High Temperature Aging
The present work adresses the evaluation of modified 9Cr-1Mo steels magneic hystersis loop and magnetic Barkhsuen emission techniques for the samples subjected to high temperature ageing for different durations. The initially quenched and then tempered material revealed different magnetic behaiour with ageing. The relxation of stresses and reduction of high value of dislocations due to quenchin...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Materials Research
سال: 2011
ISSN: 2195-8556,1862-5282
DOI: 10.3139/146.110603