High Temperature Solid State Reaction of Cobalt-Lanthanum-Alumina NOx Removal Composite Catalyst
نویسندگان
چکیده
منابع مشابه
SOLID STATE REDUCTION OF CHROMITE IN HIGH CARBON FERROCHROMIUM-CHROMITE COMPOSITE PELLETS
Abstract: In this paper solid state reduction of high carbon ferrochromium-chromite composite pellets in the temperature range of 900-1350°C was investigated. A two stage reduction mechanism is proposed. The first stage is likely to be controlled by the chemical reaction with activation energy of 127.2kJ/mol. In the second stage, solid state diffusion of carbon through the reaction product ...
متن کاملNovel nanowire-structured polypyrrole-cobalt composite as efficient catalyst for oxygen reduction reaction
A novel nanowire-structured polypyrrole-cobalt composite, PPy-CTAB-Co, is successfully synthesized with a surfactant of cetyltrimethylammounium bromide (CTAB). As an electro-catalyst towards oxygen reduction reaction (ORR) in alkaline media, this PPy-CTAB-Co demonstrates a superior ORR performance when compared to that of granular PPy-Co catalyst and also a much better durability than the comme...
متن کاملEfficient Removal of Methylene Blue by Fenton-like Reaction using nZVI/GAC Composite as Catalyst
A composite of nano-zerovalent iron (nZVI) supported on granular activated carbon (GAC) was synthesizedthrough adsorption-reduction method, and its performances used as catalyst of Fenton-like were investigated to degrade methylene blue (MB) in model wastewater.Theresults show thathomogeneous dispersion of nZVI was greatly improved after supported on GAC. In comparison, the composite (nZVI/GAC)...
متن کاملPreparation of lanthanum- p-alumina with high surface area by a homogeneous precipitation method for use as catalyst support
Samples containing mixtures of 5 mol % La203 and 95 mol % Al203 were prepared by homogeneous precipitation method with or without the presence of various anions, and calcined at different temperatures in the range of 873-1473 K. Sample prepared by urea hydrolysis in the absence of anions, and calcined at about 1273 K results in the formation of pure lanthanum-,8-alumina (LBA) with high surface ...
متن کاملSynthesis & Characterization of CaB4O7 Powder by Solid-State Reaction
The synthesis of calcium tetraborate was investigated in a temperature ranging from 800℃ to 900℃ using the solid-state reaction method. The synthesis was done using ammonium tetraborate tetrahydrate as the source of boron. At temperatures of 800 ℃ and 880 ℃, the mixed phases from different compounds were formed. At the optimum temperature of 840℃, the mixed phase was only composed of meta and t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 2004
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.51.86