High-temperature oxidation of NiCr alloys with small amounts of rare earth elements (Y, Lu)
نویسندگان
چکیده
منابع مشابه
High Temperature Erosion- Oxidation Behavior of Nickel- Based Alloys Containing Mo in Fluidized Bed Waste Incineration
High-temperature erosion-oxidation behavior of nickel-based alloys containing 0-7 wt.% Mo in fluidized bed waste incineration conditions was studied. A stream of hot condensed air with a flow rate of 25 L/min caused hot silica sand (700 °C) mixed with 0.5 wt.% of chloride salts to hit the specimens for 250 h. By removing the erosive factor, the high-temperature oxidation behavior of the alloys ...
متن کاملRare Earth Elements Profile
Definitions and characteristics The rare earth elements (REE) (sometimes referred to as the rare earth metals) are a group of 17 chemically similar metallic elements, including the 15 lanthanides, scandium and yttrium. The lanthanides are elements spanning atomic numbers 57 (lanthanum, La) to 71 (lutetium, Lu) (Table 1). The lanthanides all occur in nature, although promethium, the rarest, only...
متن کاملRare earth elements complexation with humic acid
HAL is a multi-disciplinary open access archive for the deposit and dissemination of scientific research documents, whether they are published or not. The documents may come from teaching and research institutions in France or abroad, or from public or private research centers. L’archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau...
متن کاملNew Techniques for the Synthesis of Metals and Alloys
Two major areas of effort are encompassed: I. New Techniques for the Synthesis of Metals and Alloys The High Rate Physical Vapor Deposition (HRPVD) process is to be used for the following: 1. Preparation and characterization of Ni and Ni-20Cr alloy sheet 2. Synthesis of compounds Y-O., TiC, Si^N, by reactive evaporation and their characterization 3. Dispersion strengthened alloys, Ni-ZOCr-Y-O ,...
متن کامل- Based Rare - Earth - Free Permanent - Magnet Alloys
This study presents the structural and magnetic properties of melt-spun , , and alloys. Appreciable permanent-magnet properties with a magnetocrystalline anisotropy of about 9.6–16.5 , a magnetic polarization –10.6 kG, and coercivities –3.0 kOe were obtained by varying the composition of these alloys. Structural analysis reveals that the positions of x-ray diffraction peaks of show good agreeme...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Advanced Science
سال: 2008
ISSN: 1881-3917,0915-5651
DOI: 10.2978/jsas.20.16