High-Temperature Oxidation of Ni Bearing Low-Alloy Steels in the Air
نویسندگان
چکیده
منابع مشابه
AN INVESTIGATION TO BAINITE FORMATION MORPHOLOGIES IN NI-CR BEARING LOW CARBON STEELS THROUGH THERMOMECHANICAL PROCESSING
The presence of bainite in the microstructure of steels to obtain a proper combination of strength and toughness has always been desired. The previous works however have shown that the presence of preferred bainite morphologies in the microstructure of any steel would not be readily accessible. In addition, the appearance of different bainite morphologies in the microstructure of any steel is d...
متن کاملEstimation of Atmospheric Corrosion of High-Strength, Low-Alloy Steels
This data analysis was undertaken to investigate the weatherability of steels whose compositions do not fall in the range of ASTM Standard G101, Estimating the Atmospheric Corrosion Resistance of Low-Alloy Steels (1). This standard was developed to estimate the corrosion resistance of low-alloy weathering steels from chemical composition data and from actual atmospheric exposure tests. This sta...
متن کاملHigh Temperature Oxidation Behaviour of Nimonic - 115 Alloy in Presence of Sodium Salts at 850OC
The high temperature oxidation behaviour of Nimonic-115 industrial alloy has been investigated in presence of NaNO3, Na2CO3 and Na2O2 at 850oC in flowing air. The oxidation kinetics and effect of salt deposition for the period of 48 h were studied. The scale morphologies were determined on the basis of X-ray diffraction anal...
متن کاملTHE OXIDATION RESISTANCE OF HIGH ALUMINUM HEAT RESISTANT STEELS
Abstract: In this research, the oxidation behaviour of high Aluminum heat resistant steel (%25Cr,%20Ni,%8Al) hasbeen evaluated at the temperature range of (1000-1300ºC).The results showed that there was no countinous healinglayer on the surface of the alloy when Al increased up to %5.5 and the oxidation resistance of steel decreased due toformation of spinel oxides on the surface.By increasing ...
متن کاملDetermining the Hot Deformation Temperature Range of Medium Carbon Ni-Cr-Mo Low Alloy Steels using Hot Tensile and Hot Torsion Tests
The aim of this study was to investigate the suitable temperature range for hot deformation of three medium carbon Ni-Cr-Mo low alloy steels by hot tensile and hot torsion tests. Hot tensile tests were carried out in the te,prature range of 850-1150°C at a constant strain rate of 0.1 s-1 until fracture. Then, the tensile flow behavior, hot ductility and microstructural evolution of the steels w...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1996
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.82.7_564