High-temperature oxidation of Al2O3-forming heat-resistant alloys with small amount of sulfur at 1373 and 1473K.
نویسندگان
چکیده
منابع مشابه
On High-Temperature Behaviours of Heat Resistant Austenitic Alloys
Advanced heat resistant materials are important to achieve the transition to long term sustainable power generation. The global increase in energy consumption and the global warming from greenhouse gas emissions create the need for more sustainable power generation processes. Biomass-fired power plants with higher efficiency could generate more power but also reduce the emission of greenhouse g...
متن کاملTHE OXIDATION RESISTANCE OF HIGH ALUMINUM HEAT RESISTANT STEELS
Abstract: In this research, the oxidation behaviour of high Aluminum heat resistant steel (%25Cr,%20Ni,%8Al) hasbeen evaluated at the temperature range of (1000-1300ºC).The results showed that there was no countinous healinglayer on the surface of the alloy when Al increased up to %5.5 and the oxidation resistance of steel decreased due toformation of spinel oxides on the surface.By increasing ...
متن کاملHigh Temperature Erosion- Oxidation Behavior of Nickel- Based Alloys Containing Mo in Fluidized Bed Waste Incineration
High-temperature erosion-oxidation behavior of nickel-based alloys containing 0-7 wt.% Mo in fluidized bed waste incineration conditions was studied. A stream of hot condensed air with a flow rate of 25 L/min caused hot silica sand (700 °C) mixed with 0.5 wt.% of chloride salts to hit the specimens for 250 h. By removing the erosive factor, the high-temperature oxidation behavior of the alloys ...
متن کاملcomparison of the amount of debris extruded apically in two rotary techniques: flexmaster and m2
چکیده ندارد.
15 صفحه اولHigh Temperature Oxidation Behaviour of Nimonic - 115 Alloy in Presence of Sodium Salts at 850OC
The high temperature oxidation behaviour of Nimonic-115 industrial alloy has been investigated in presence of NaNO3, Na2CO3 and Na2O2 at 850oC in flowing air. The oxidation kinetics and effect of salt deposition for the period of 48 h were studied. The scale morphologies were determined on the basis of X-ray diffraction anal...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Advanced Science
سال: 2000
ISSN: 1881-3917,0915-5651
DOI: 10.2978/jsas.12.89