High-temperature oxidation behaviour of refurbished (Ni,Pt)Al coating on Ni-based superalloy at 1100 °C
نویسندگان
چکیده
A single-phase (Ni,Pt)Al coating was removed by soft chemical stripping method successfully after preceding oxidation at 1100 °C for 300 h, and a fresh one refurbished subsequently. Oxidation behaviour of the studied in comparison with virgin °C. The results show that exhibited superior isothermal cyclic resistance than terms rate surface rumpling. effects roughness residual elements on rate, rumpling interdiffusion were discussed.
منابع مشابه
Simulation of oxidation-nitridation-induced microstructural degradation in a cracked Ni- based superalloy at high temperature
In turbine engines, high temperature components made of superalloys may crack in a creep process during service. With the inward flux of the gases, e.g. oxygen and nitrogen, along those cracks, the microstructure of the superalloy substrate nearby the cracks may degrade by internal oxidation and nitridation. The aim of this study is to investigate and simulate the oxidation-nitridation-induced ...
متن کاملThe effect of yttria coatings on the oxidation behaviour of Fe-25Al and Ni-32Al at 1100 and 1200 °C
The influence of Y 2 0 3 coatings on the oxidation behaviour of Fe-25wt%Al and Ni-32wt%Al has been investigated at 1100 and 1200 OC. Samples were sputter coated with 4 nm of Y 2 0 3 and oxidized sequentially in 1602 and Oxide scales have been characterized using SIMS, XPS, SEM, X-ray and electron diffraction. A comparison is made between the growth of oxide on Y203-coated and uncoated alloys. T...
متن کاملNickel Base Superalloy Rene®80 – The Effect of High Temperature Cyclic Oxidation on Platinum-Aluminide Coating Features
Nickel base superalloy alloys are used in the manufacture of gas turbine engine components, which in use are exposed to high temperatures and corrosive environments. The platinum aluminide coatings described here have been developed to protect nickel base superalloy alloys from oxidation. In this study, the effect of cyclic oxidation, platinum layer thickness and aluminizing process on beha...
متن کاملHigh Temperature Oxidation Behaviour of Nimonic - 115 Alloy in Presence of Sodium Salts at 850OC
The high temperature oxidation behaviour of Nimonic-115 industrial alloy has been investigated in presence of NaNO3, Na2CO3 and Na2O2 at 850oC in flowing air. The oxidation kinetics and effect of salt deposition for the period of 48 h were studied. The scale morphologies were determined on the basis of X-ray diffraction anal...
متن کاملOxidation behaviour of simple and Pt-modified aluminide coatings on IN738 at 1100 °C
The oxidation of both low and high-activity simple and Pt-modified aluminide coatings on nickel base superalloy IN738 has been studied in static air at 1100 OC up to 1000 h. For all coatings oxidation followed a parabolic law up to 400 h. The two Pt-modified coatings showed better protectiveness with lower mass gains and smaller rate constants, especially for long reaction times. The presence o...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Corrosion Science
سال: 2021
ISSN: ['1879-0496', '0010-938X']
DOI: https://doi.org/10.1016/j.corsci.2021.109521