High-temperature Oxidation Behavior and Scale Morphology of Si-containing Steels
نویسندگان
چکیده
منابع مشابه
High Temperature Behavior of Dual Phase Steels
Dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500C. Stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500C, and smooth flow at the other temperatures. Both yield and ultimate tensile strengths increased with increasing testing temperature up to about 450<sup...
متن کاملHigh Temperature Erosion- Oxidation Behavior of Nickel- Based Alloys Containing Mo in Fluidized Bed Waste Incineration
High-temperature erosion-oxidation behavior of nickel-based alloys containing 0-7 wt.% Mo in fluidized bed waste incineration conditions was studied. A stream of hot condensed air with a flow rate of 25 L/min caused hot silica sand (700 °C) mixed with 0.5 wt.% of chloride salts to hit the specimens for 250 h. By removing the erosive factor, the high-temperature oxidation behavior of the alloys ...
متن کاملhigh temperature behavior of dual phase steels
dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500c. stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500c, and smooth flow at the other temperatures. both yield and ultimate tensile strengths increased with increasing testing temperature up to about 4500c and then decreased at h...
متن کاملTHE OXIDATION RESISTANCE OF HIGH ALUMINUM HEAT RESISTANT STEELS
Abstract: In this research, the oxidation behaviour of high Aluminum heat resistant steel (%25Cr,%20Ni,%8Al) hasbeen evaluated at the temperature range of (1000-1300ºC).The results showed that there was no countinous healinglayer on the surface of the alloy when Al increased up to %5.5 and the oxidation resistance of steel decreased due toformation of spinel oxides on the surface.By increasing ...
متن کاملThe Study of High Temperature Oxidation behavior of Different Microstructures of HVOF Thermally Sprayed Coatings
Improvement of thermally sprayed coating properties by microstructure modification has been considered as a significant solution. Therefore, in this research the effect of dissolved oxygen content and post heat treatment on the formation and distribution of secondary phase particles, particularly in nano-scale in the coatings during spraying and after that were studied. Ni-5 wt% Al powders were...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ISIJ International
سال: 2007
ISSN: 0915-1559,1347-5460
DOI: 10.2355/isijinternational.47.1329