High temperature bi-axial low cycle fatigue behaviour of railway wheel steel
نویسندگان
چکیده
منابع مشابه
Identification of Low Cycle Fatigue Parameters of High Strength Low-alloy (hsla) Steel at Room Temperature
S. Bulatović, Yugoslav River Shipping, Serbia, Lj. Milović, University of Belgrade, Faculty of Technology and Metallurgy, Serbia, A. Sedmak, University of Belgrade, Faculty of Mechanical Engineering, Serbia, I. Samardžić, University of Osijek, Mechanical Engineering Faculty, Slavonski Brod, Croatia Low cycle fatigue test was performed in ambient atmosphere at room temperature. Cycle loading of ...
متن کاملHigh-Cycle Microscopic Corrosion Fatigue Behavior and Life Prediction of 25CrMo Steel Used in Railway Axle
The effects of environmental media on the corrosion fatigue fracture behavior of 25CrMo steel were investigated. The media include air, and a 3.5 wt.% and a 5.0 wt.% NaCl solutions. Experimental results indicate that the media induces the initiation of corrosion fatigue cracks at multiple sites. The multi-cracking sites cause the changes in the crack growth directions, the crack growth rate dur...
متن کاملEnergy-Based Prediction of Low-Cycle Fatigue Life of CK45 Steel and SS316 Stainless Steel
In this paper, low cycle fatigue life of CK45 steel and SS316 stainless steel under strain-controlled loading are experimentally investigated. In addition, the impact of mean strain and strain amplitude on the fatigue life and cyclic behavior of the materials are studied. Furthermore, it is attempted to predict fatigue life using energy and SWT damage parameters. The experimental results demons...
متن کاملHigh Cycle Fatigue Property of Carburized 20Cr Gear Steel under Axial Loading
Abstract: The high cycle fatigue property of carburized 20Cr gear steel was experimentally investigated under axial loading with a stress ratio of zero. The test results show that this steel exhibits gradually decreasing S-N characteristics, and the fatigue strength corresponding to 109 cycles is about 455 MPa. Based on the observation of fracture surfaces, the interior inclusion fisheye-induce...
متن کاملLow-Cycle Fatigue Behaviour of AISI 18Ni300 Maraging Steel Produced by Selective Laser Melting
Selective laser melting has received a great deal of attention in recent years. Nevertheless, research has been mainly focused on the technical issues and their relationship with the final microstructure and monotonic properties. Fatigue behaviour has rarely been addressed, and the emphasis has been placed on high-cycle regimes. The aim of this paper is, therefore, to study, in a systematic man...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATEC Web of Conferences
سال: 2019
ISSN: 2261-236X
DOI: 10.1051/matecconf/201930007001