High Current Density Electrodeposition of Ni-P Alloy Film on Alumina Plate.
نویسندگان
چکیده
منابع مشابه
Preparation of Ni-Co Alloy Foils by Electrodeposition
Electrodeposition of Ni-Co alloy foils on titanium substrate was performed in an acid chloride-sulphate bath. The influences of electrodeposition parameters such as current density, temperature, pH value, cobalt sulphate and saccharin concentration on composition and current efficiency were investigated in detail. The morphology and the microstructure of deposits were analyzed by SEM and XRD, r...
متن کاملHigh current density electrodeposition from silver complex ionic liquids.
Liquid metal salts are electrolytes with the highest possible metal concentration for electrodeposition, because the metal ion is an integral part of the solvent. This paper introduces the new ionic silver complexes [Ag(MeCN)(4)](2)[Ag(Tf(2)N)(3)], [Ag(MeCN)][Tf(2)N] and [Ag(EtIm)(2)][Tf(2)N], where MeCN stands for acetonitrile, EtIm for 1-ethylimidazole and Tf(2)N is bis(trifluoromethylsulfony...
متن کاملEffect of current density on the microstructure and polarization resistance of Ni-P-TiO2-ZrO2 composite coating
Composite coatings with nickel matrix and ceramic reinforcement particles have high ability to improve surface properties, such as good corrosion and abrasion resistance. In this study, Ni-P composite coating was coated with ZrO2 and TiO2 ceramic particles on the AISI 316 steel substrate through direct current plating method. The effect of the current densities of 20, 30, 40 and 50 mA/cm2 on th...
متن کاملCathodic Electrodeposition and Characterization of YAG Nanostructure: Effect Current Density on the Morphology
Abstract YAG (Yttrium Aluminum Garnet) was successfully prepared through cathodic electrodeposition process using applying different current densities to the mixture of YCl3 and AlCl3 dissolved in water/ethanol 1:1 solution. Hydroxide precursors were cathodically grown on the cathode surface (at different current densities) and then the obtained hydroxide powder was heat-treated at 1100 °...
متن کاملInfluence of magnetic field on the electrodeposition of Ni–Co alloy
The electrodeposition of Ni–Co alloy from a nickel Watt’s solution in the absence and presence of a permanent parallel magnetic field (PPMF) to the plane of deposition (perpendicular to direction of current) produced a deposited layer with mostly fine grain structure. The deposited layers have been characterized by scanning electron microscopy (SEM) and energy dispersive X-ray (EDX). It was fou...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1996
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.45.572