Heat treatment of a direct composite resin: influence on flexural strength
نویسندگان
چکیده
منابع مشابه
Heat treatment of a direct composite resin: influence on flexural strength.
The purpose of this study was to evaluate the flexural strength of a direct composite, for indirect application, that received heat treatment, with or without investment. One indirect composite was used for comparison. For determination of the heat treatment temperature, thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) were performed, considering the initial weight l...
متن کاملEffect of radiotherapy on the radiopacity and flexural strength of a composite resin.
The aim of this study was to evaluate the effect of radiotherapy on the radiopacity and flexural strength of composite resin. Forty Z250 composite resin specimens were polymerized using a halogen light-curing unit and divided into 5 groups, in accordance with the radiotherapy dose: G1- without irradiation, G2- 30 Gy, G3- 40 Gy, G4- 50 Gy and GS- 60 Gy Digital images were obtained using a GE 100...
متن کاملThe effect of specimen dimensions on the flexural strength of a composite resin.
UNLABELLED PUORPOSE: The aim of this study was to evaluate the effect of specimen dimensions on the flexural strength of a composite resin (Heliomolar RO). METHODS The different dimensions tested - length x width x height (mm) were: 25x2x4; 25x2x2 (ISO 4049); 15x2x2; 10x2x2 and 10x2x1. Light-curing was performed at 600 mW/cm² for 40s, three times along the 25mm specimens, twice along 15mm spe...
متن کاملEffect of carbamide peroxide bleaching gel on composite resin flexural strength and microhardness.
This study investigated the effect of 16% carbamide peroxide (Whiteness Perfect/FGM) on the Vickers microhardness and flexural strength of the restorative composites Filtek Z100 (hybrid), Filtek Z350 (nanofill), Brilliant (micro-hybrid) and Opallis (micro-hybrid). Disc-shaped (4x2 mm; n=5) and bar-shaped (12x2x1 mm; n=10) specimens of each restorative material were randomly divided into 2 group...
متن کاملDevelopment of metal-resin composite restorative material. Part 4. Flexural strength and flexural modulus of metal-resin composite using Ag-In alloy particles as filler.
The flexural strength and flexural modulus of an experimental metal-resin composite, which used Ag-In alloy particle as the filler, were evaluated. The effect of acid treatment and heat treatment on the Ag-In alloy particle was investigated. The flexural strength of the experimental metal-resin composites ranged from 65.5 MPa to 91.0 MPa. The flexural strength of the metal-resin composite incre...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Brazilian Oral Research
سال: 2009
ISSN: 1806-8324
DOI: 10.1590/s1806-83242009000300004