Heat capacity and thermodynamic functions of γ-Al2O3
نویسندگان
چکیده
منابع مشابه
Heat Capacity and Thermodynamic Functions of Ni36Nb24Zr40 Glassy Alloy
The heat capacity of a Ni36Nb24Zr40 glassy alloy was measured by adiabatic calorimetry from 13 to 300K. The smoothed values of molar heat capacity were calculated from the data using a least-squares method. The standard enthalpy, entropy, and Gibbs energy were calculated from the smoothed heat capacity values. Assuming Hð0Þ 1⁄4 0 and Sð0Þ 1⁄4 0 at 0K, the heat capacity, enthalpy, entropy, and G...
متن کاملA numerical investigation of γ-Al2O3-water nanofluids heat transfer and pressure drop in a shell and tube heat exchanger
The effect of γ-Al2O3 nanoparticles on heat transfer rate, baffle spacing and pressure drop in the shell side of small shell and tube heat exchangers was investigated numerically under turbulent regime. γ-Al2O3-water nanofluids and pure water were used in the shell side and the tube side of heat exchangers, respectively. Since the properties of γ-Al2O3-water nanofluids were variable, they were ...
متن کاملLow Temperature Heat Capacity and Thermodynamic Properties of Zinc Ferrite*
The heat capacity of zinc ferrite (ZnFe,O,) has been determined over the range 5 to 350°K. Molal values of C~,S’, and HO-H,O computed from the thermal data are 32,99&t-0.03 cal/deg., 36.01 f0.03 cal/deg., and 18,00&0.02 Cal, respectively, at 298,lS”K. A co-operative thermal anomaly associated with antiferromagnetic ordering occurs at 9.5” and extends toward higher temperatures probably as a con...
متن کاملa numerical investigation of γ-al2o3-water nanofluids heat transfer and pressure drop in a shell and tube heat exchanger
the effect of γ-al2o3 nanoparticles on heat transfer rate, baffle spacing and pressure drop in the shell side of small shell and tube heat exchangers was investigated numerically under turbulent regime. γ-al2o3-water nanofluids and pure water were used in the shell side and the tube side of heat exchangers, respectively. since the properties of γ-al2o3-water nanofluids were variable, they were ...
متن کاملProduction of γ-Al2O3 from Kaolin
The paper reports a process for synthesis of γ-alumina from kaolin. Kaolin was transformed to meta-kaolin by calcination at 800 ̊C for 2h. γ-alumina powder was synthesized through extracting alumina from metakaolin via H2SO4 and meta-kaolin reactions and consequently precipitation in ethanol, which led to form the aluminum sulfate. The precipitated aluminum sulfate was dried and calcined at 900 ̊...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: The Journal of Chemical Thermodynamics
سال: 2017
ISSN: 0021-9614
DOI: 10.1016/j.jct.2017.04.011