Hardening Embrittlement and Non-Hardening Embrittlement of Welding-Heat-Affected Zones in a Cr-Mo Low Alloy Steel
نویسندگان
چکیده
منابع مشابه
Radiation Effects in Metals: Hardening, Embrittlement, and Fracture 18.1 STRUCTURAL N!ETALS FOR FAST REACTORS
The neutron eccmomy of a fast reactor is not so significantly affected by neutron capture in the structural materials in the core as is that of a thermal reactor. First, most neutron-capture cross sections increase with de creasing neutron energy, and the neutron population of the liquid-metal fast breeder reactor (Lhl FI~R) contains a far lower percentage of thermal neutrons than does that (I...
متن کاملEmbrittlement of Al-Li-Cu-Mg alloys at slightly elevated temperatures: microstructural mechanisms of hardening
When underaged, damage tolerant Al-Li based alloys are exposed to slightly elevated temperatures (60 to 100oC), their strength increases and toughness decreases. To study the first stages of this process, 8090 sheet in three underaged heat treatment conditions, including T3, T81 and a multistage temper, was exposed for 1000 h at 70°C. Using a model for strengthening in combination with a quanti...
متن کاملExperimental Studies on the Microstructure and Hardness of Laser Transformation Hardening of Low Alloy Steel
An experimental investigation with Nd:YAG laser system was carried out to study the effects of laser hardening process parameters on the microstructure and hardness during laser hardening of EN25 steel. The laser beam is allowed to scan on the surface of the work piece by varying the laser beam power (750–1250 W) and travel speed (500–1000 mm/min) of the work table. The microstructural features...
متن کاملPrecipitation hardening in a dental low-gold alloy.
Age-hardening characteristics in a dental low-gold alloy composed of 40.0 wt% Au-35.0 wt% Ag-7.9 wt% Pd-7.0 wt% Cu-5.0 wt% In-3.5 wt% Zn-1.5 wt% Sn, were investigated by means of the hardness test, XRD study, SEM observations and EPMA. The following results were obtained. The age-hardening was characterized by a precipitation of Cu-rich alpha2 phase in the a phase. The softening that occurred f...
متن کاملPitting-induced hydrogen embrittlement of magnesium- aluminium alloy
In this study, the pitting corrosion susceptibility and its role on the hydrogen embrittlement behavior of AZ80 magnesium alloy were studied using slow strain rate testing (SSRT), electrochemical technique and immersion test method. The electrochemical and immersion tests in chloride-containing solution revealed severe pitting corrosion in the alloy. The SSRT results of the alloy under continuo...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metals
سال: 2018
ISSN: 2075-4701
DOI: 10.3390/met8060405