Hard magnetic properties of melt-spun Mn-Al-C alloys
نویسندگان
چکیده
منابع مشابه
Hard magnetic properties of melt-spun Mn-Al-C alloys
Structural and magnetic characterization of Mnx−yAl100−x−yC2y (x = {50, 55}; y = {0, 1}) melt-spun ribbons is reported. To obtain the metastable ferromagnetic τ-phase, rapidly solidified alloys were annealed either in a vacuum furnace at 823 K or directly in the vibrating sample magnetometer under applied magnetic field. Optimal magnetic properties were demonstrated by Mn54Al44C2 samples proved...
متن کاملMagnetic properties and giant magnetoresistance in melt-spun Co-Cu alloys
Magnetic, structural, and transport properties of as-quenched and annealed ColOCugO samples have been investigated using x-ray diffraction and a SQUID magnetometer. The largest value of MR change was observed for the as-quenched sample annealed at 450 “C for 30 min. The magnetic and transport properties closely correlate with the microstructure, mainly with Co magnetic particle size and its dis...
متن کاملMagnetic properties and synthesis conditions of Nd2Fe23B3 melt-spun alloy
The formation of amorphous and crystalline state of the Nd2Fe23B3 alloy from melt-spun ribbon is presented. The synthesis conditions are investigated combining DSC, X-ray diffraction and thermomagnetic analysis. The thermomagnetic analysis is found to be very useful to optimize the synthesis process. Comparison of these results enables to discuss the thermal stability of both the amorphous and ...
متن کاملThe Structure and Magnetic Properties of Co77Zr18W5 Melt-Spun Ribbons
Based on X-ray diffraction, microscopic and magnetic analysis, the structure and magnetic properties of Co77Zr18W5 melt-spun ribbons were studied in this paper. A new element to stabilize the metastable Co5Zr phase was found and the coercivity observed in Co-Zr alloys can be obviously enhanced by proper tungsten substitution. The Curie temperature of Co77Zr18W5 ribbons is 475 ̊C which suggests t...
متن کاملRecrystallization Phenomena in Melt-Spun (Fe100- xVx)75P15C10 Alloys
(Fe100-xVx)75P15C10 (x=0, 5, 10 and 15) semiamorphous alloys were prepared by the melt spinning technique and their structural, thermal and magnetic properties were investigated. The structure of the alloys was studied by X-ray diffraction (XRD) for annealing temperatures of 400 oC to 650 oC within a 30 minute annealing time. The XRD patterns show that the samples contain a BCC structure for te...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: EPJ Web of Conferences
سال: 2013
ISSN: 2100-014X
DOI: 10.1051/epjconf/20134006008