Growth characteristics of primary M7C3 carbide in hypereutectic Fe-Cr-C alloy
نویسندگان
چکیده
منابع مشابه
Growth characteristics of primary M7C3 carbide in hypereutectic Fe-Cr-C alloy
The microstructure of the hypereutectic Fe-Cr-C alloy is observed by optical microscopy (OM). The initial growth morphology, the crystallographic structure, the semi-molten morphology and the stacking faults of the primary M7C3 carbide are observed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The in-suit growth process of the primary M7C3 carbide was observe...
متن کاملStability of eutectic carbide in Fe-Cr-Mo-W-V-C alloy
The stability of the eutectic carbide in a self-designed Fe-Cr-Mo-W-V-C alloy during solidifi atio as a alyzed i this ork. The ar ide pre ipitatio rule of the steel was calculated by Thermo-Calc.The typical microstructures at 1240 °C and 1200 °C ere o ser ed y opti al i ros ope OM ,field e issio s a i g ele tro microscope (FESEM) and transmission electron microscope (TEM). The selected area dif...
متن کاملControl of eta carbide formation in tungsten carbide powders sputter-coated with (Fe/Ni/Cr)
Composite powders of tungsten carbide with variable coating contents of Fe/Ni/Cr based alloys (1–15 wt.%) were prepared by sputtering. The coated powders have revealed a good performance to shape-forming and sintering. However, the presence of nanocrystalline coatings could enhance the formation of a brittle phase during sintering, named g-phase, (M,W)6C. To investigate this effect, the powders...
متن کاملEvolution of magnetization reversal mechanism in Fe-Cr alloy films
A large thin film sample of FexCr1−x alloy with a composition gradient x=0.38−0.52 has been prepared by co-sputtering to investigate magnetic anisotropy and magnetization effects on reversal mechanisms. The single-phased Fe-Cr films have a bcc structure with 110 preferred orientation. Since the magnetization decreases as the Fe content is decreased and the uniaxial anisotropy energy keeps at al...
متن کاملCharacteristics of Fe-Cr-Al Alloy Nanopowders Prepared by Electrical Wire Explosion Process under Liquid Media
Fe-Cr-Al alloy nanopowders were successfully prepared by electrical wire explosion method in ethyl alcohol media. The formation of FeCr-Al alloy nanopowder was monitored by X-ray diffraction. The alloy powders have spherical shape and nanometer size. The alloy powders prepared by the electrical wire explosion method have main crystal structures of bcc Fe-Cr alloy. The geometric mean diameter an...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Scientific Reports
سال: 2016
ISSN: 2045-2322
DOI: 10.1038/srep32941