Grain Structure and Microhardness Development of Twin-Roll Cast Aluminum Strips after Constrained Groove Pressing

Mechanical Behaviour of Pure Aluminum Processed by Constrained Groove Pressing

In recent years, the fabrication of bulk materials with ultra fine grain sized materials processed by SPD methods. Different techniques have been used to introduce large plastic strains in to bulk metals such as Equal Channel Angular Pressing (ECAP) [1-3], Accumulative Roll Bonding (ARB) [4-7], Repetitive Corrugation and Straitening (RCS) [8,9], Constrained Groove Pressing (CGP) [5] and Constra...

High Temperature Deformation of Twin-Roll Cast Al-Mn-Based Alloys after Equal Channel Angular Pressing

Twin roll cast Al-Mn- and Al-Mn-Zr-based alloys were subjected to four passes of equal channel angular pressing. The resulting grain size of 400 nm contributes to a significant strengthening at room temperature. This microstructure is not fully stable at elevated temperatures and recrystallization and vast grain growth occur at temperatures between 350 and 450 °C. The onset of these microstruct...

The Influence of Silicon Content on Recrystallization of Twin-Roll Cast Aluminum Alloys for Heat Exchangers

An investigation on the bond strength of aluminum strips in presence of brass mesh after cold roll bonding

In the present study, the presence of brass mesh on the bond strength of aluminum (AA1050) strips in the cold roll bonding process was investigated. The influence of various process parameters including reduction in thickness, pre-rolling annealing, initial thickness of the strips, and post-rolling annealing was also considered. After cold roll bonding process, peeling test was carried out and ...

Annealing Effects in Twin-Roll Cast AA8006 Aluminium Sheets Processed by Accumulative Roll-Bonding

Ultrafine grained sheets were prepared from a twin-roll cast AA8006 aluminium alloy using accumulative roll-bonding process at room temperature. The evolution of microstructure of sheets after three accumulative roll-bonding passes during isochronal annealing with a constant step of 20 °C/20 min was studied by light and electron microscopy. The influence of the resulting microstructure on mecha...