Grain growth behaviour of an AISI 422 martensitic stainless steel after hot deformation process
نویسندگان
چکیده
منابع مشابه
The Effect of Hot Deformation Parameters on Grain Size Refinement in a Martensitic Stainless Steel
The grain size refinement of AISI 422 martensitic stainless steel in the temperature range of 950-1150 ºC was investigated by hot deformation tests. The deformed specimens were held at deformation temperature with delay times of 5 to 300s after achieving a strain of 0.3. The austenite grains exhibit a considerable growth at temperature higher than 1050˚C, while the grain coarsening is negligibl...
متن کاملGrain Size Effect on the Hot Deformation Processing Map of AISI 304 Austenitic Stainless Steel
In this study, the hot deformation processing map of AISI 304 austenitic stainless steel in two initial grain sizes of 15 and 40 μm was investigated. For this purpose, cylindrical samples were used in the hot compression test at the temperature range of 950-1100 °C and the strain rate of 0.005-0.5% s-1. At first, the relationship between the peak stress and Zener-Hollomon parameter w...
متن کاملPREDICTION OF HOT DEFORMATION BEHAVIOUR OF A PH STAINLESS STEEL AT HIGH STRAIN RATES
In this study the hot deformation behaviour of a precipitation hardened (PH) stainless steel at high strain rates has been predicted through hot compression testing. Stress-strain curves were obtained for a range of strain rates from 10-3 to 10+1 S-1 and temperatures from 850 to 1150°C. Results obtained by microstructure and stress-strain curves show that at low temperatures and high strain rat...
متن کاملEvaluating Wear Properties of AISI 420 Martensitic Stainless Steel after Laser Transformation Hardening
As the turbine industries need to manufacture turbine blades made of martensitic stainless steel AISI 420 with high toughness and wear resistance, local laser hardening has become more and more important. In this research, surface of the samples was initially hardened by high-power pulsed laser beam; then, optimum parameters of hardening were calculated and wear resistance of surface hardened s...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Canadian Metallurgical Quarterly
سال: 2018
ISSN: 0008-4433,1879-1395
DOI: 10.1080/00084433.2018.1444414