Grain Growth Behavior of YIG Sintered Ferrites.
نویسندگان
چکیده
منابع مشابه
Grain growth kinetic of spark plasma sintered magnesia
In this research, the densification of magnesia nanopowder with a mean particle size of about 100 nm was investigated by spark plasma sintering undera pressures of 80 MPa and at temperature range from 1000 °C to 1400 °C and a heating rate of 50 °C/min for 20 minutes. The density of the samples slowly increased with increasing sintering temperatures to 1200 °C. Afterwards, with more increasing o...
متن کاملDeformation and Grain Growth of Low-Temperature-Sintered High-Purity Alumina
9 = 0.6 I / s ' 7 = 6.0 0 7 = 2 4 i ti 3 = 6 0 Through close control over green-state powder processing, pure alumina ceramics of 0.5-pm grain size were obtained by sintering at 1250°C. The static grain growth of this material was modest at temperatures below 1300°C. However, dynamic grain growth occurred rapidly during superplastic deformation. Therefore, although the ultrafine-grained alumina...
متن کاملDamage Behavior of Sintered Fiber Felts
The reduction of aircraft noise is important due to a rising number of flights and the growth of urban centers close to airports. During landing, a significant part of the noise is generated by flow around the airframe. To reduce that noise porous trailing edges are investigated. Ideally, the porous materials should to be structural materials as well. Therefore, the mechanical properties and da...
متن کاملSynthesis and Thermoelectric Behavior in Nanoparticles of Doped Co Ferrites
Samples of CoFe2-xCrxO4 where x varies from 0.0 to 0.5 were prepared by co-precipitation route. These samples were sintered at 750°C for 2 hours. These particles were characterized by X-ray diffraction (XRD) at room temperature. The FCC spinel structure was confirmed by XRD patterns of the samples. The crystallite sizes of these particles were calculated from the most intense peak by Scherrer f...
متن کاملRelation Between Firing Conditions Grain Boundary Structure and Magnetic Properties in Polycrystalline MnZn-Ferrites
The influence of the firing conditions on the nanoscale structure of the grain boundaries and on the magnetic properties of polycrystalline MnZn-ferrites is investigated, on specimens of nearly identical microstructures. High oxygen partial pressures favor accumulation of impurity ions at the triple points. Under appropriate oxygen pressures homogeneous accumulation of impurities along the grai...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 2001
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.48.160