Glass Waste Based Geopolymers and Their Characteristics

Inorganic polymer materials (Geopolymers) are synthesized using alumino-silicate sources as solid components with an alkaline solution. This material is used alternative for building and provides thermal protection foaming materials. paper presents the preparation of these by reaction between glass waste (from brown color bottles BP) sodium hydroxide NaOH aluminum (AN5) solutions alkali activators. For mortars (BP-N5 BP-AN5), sand was aggregate. The compressive strengths were assessed (24 6 MPa) respectively before heat treatment, hydrolytic stability (PH conductivity) tests performed. Furthermore, hardened have been heated at very high temperatures in range 200℃ to 800℃ within two hours. Based on nature behavior such materials, various variables changed; (80-140) % volume increase porosity rise through process particularly 600℃ 800℃. On other hand, (3.5-7) mass reduction occurred. It can be said that more significant different geometrical configurations (sizes shapes) considered acoustic insulation