Granite Based Glass-Ceramic Materials
In this study, production possibility of glass and glass-ceramic produced from granite was investigated. The composition of granite based glass bath mixture was 50 wt% granite, 25 wt% dolomite and 25 wt% sodium carbonate. Composition that was grounded and mixed in a ball mill for 2 h was melted at 1500 ◦C for 1 h. Glass samples were heat treated for crystallization to produce glass-ceramic mate...
متن کاملWear Properties of Gabbro Based Glass and Glass-Ceramic Materials
Glass-ceramic materials were developed from gabbro including MgO and Al2O3 additives. Heat treatments for phase transformation from glassy matrix to glass-ceramic were carried out at 1000 ◦C for 3 h. X-ray di raction studies conducted on the glass-ceramic samples revealed that the phases formed in the glass-ceramics were cordierite, anorthite, diopsitic augite, forsterite and andesine. Glass an...
متن کاملLithium Disilicate Glass-Ceramic
ceramic on light transmission of light-emitting diode (LED) and quartz-tungsten-halogen units (QTH) were evaluated. Ceramic IPS e.max CAD shades A1, A2, A3, A3.5, high (HT) and low (LT) translucency were cut (1, 2, 3, 4 and 5 mm). Light sources emission spectra were determined. Light intensity incident and transmitted through each ceramic sample was measured to determine light transmission perc...
متن کاملEFFECTS OFVARIOUS NUCLEATION AGENTS ON CRYSTALLIZATION KINETIC OFLAS GLASS CERAMIC
The effect of Y2O3, CeO2, P2O5, ZrO2 and TiO2 in single, double and triple form on crystallization mechanism of Li2OAl2O3- SiO2(LAS) glass-ceramic system was investigated .The nucleation and crystallization peak temperatures of optimized samples in each group were determined by Ray & Day method .The crystalline phase was determined by the X-ray diffractometery .The micro-structure of the sample...
متن کاملResin Cement to Glass Ceramic
silane to improve the adhesion of phosphate monomer-based (MDP) resin cement to glass ceramic. Resin and feldspathic ceramic blocks (n=48, n=6 for bond test, n=2 for microscopy) were randomly divided into 6 groups and subject to surface treatments: G1: Hydrofluoric acid (HF) 9.6% for 20 s + Silane + MDP resin cement (Panavia F); G2: HF 9.6% for 20 s + Silane + Heat Treatment (oven) + Panavia F;...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Vestnik MGSU
سال: 2014
ISSN: 1997-0935,2304-6600
DOI: 10.22227/1997-0935.2014.7.85-92