Gd/Y Hydroxide Nanosheets as Highly Efficient T1/T2 MRI Contrast Agents
نویسندگان
چکیده
منابع مشابه
Development of 153Sm-DTPA-SPION as a theranostic dual contrast agents in SPECT/MRI
Objective(s): This study describes the preparation, biodistribution of 153Sm-DTPA-SPION after intravenous injection in rats. Materials and Methods: The chelator DTPA dianhydride was conjugated to SPION using a small modification of the well-known cyclic anhydride method. Conjugation was done at a 1: 4 (SPION: ccDTPA) molar ratio. Conjugation reaction was purified with magnetic assorting column...
متن کاملSynthesis and Characterization of Chitosan Coated Manganese Zinc Ferrite Nanoparticles as MRI Contrast Agents
Manganese zinc ferrite nanoparticles (MZF NPs) were synthesized by using a direct, efficient and environmental friendly hydrothermal method. To improve the colloidal stability of MZF NPs for biomedical applications, NPs were coated with chitosan by ionic gelation technique using sodium tripolyphosphate (TPP) as crosslinker. The synthesized NPs were characterized by X ray diffraction (XRD) analy...
متن کاملHighly efficient carrier multiplication in PbS nanosheets
Semiconductor nanocrystals are promising for use in cheap and highly efficient solar cells. A high efficiency can be achieved by carrier multiplication (CM), which yields multiple electron-hole pairs for a single absorbed photon. Lead chalcogenide nanocrystals are of specific interest, since their band gap can be tuned to be optimal to exploit CM in solar cells. Interestingly, for a given photo...
متن کاملNi3+ doped monolayer layered double hydroxide nanosheets as efficient electrodes for supercapacitors.
Ni(3+) doped NiTi layered double hydroxide (NiTi-LDH) monolayer nanosheets with a particle size of ∼ 20 nm and a thickness of ∼ 0.9 nm have been successfully prepared through a facile bottom-up approach. These NiTi-LDH monolayer nanosheets exhibit excellent supercapacitor performance, including a high specific pseudocapacitance (2310 F g(-1) at 1.5 A g(-1)) and long durability compared with bul...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanomaterials
سال: 2020
ISSN: 2079-4991
DOI: 10.3390/nano11010017