Friction Stir Welding of Dissimilar Joints Between Commercially Pure Titanium Alloy and 7075 Aluminium Alloy
نویسندگان
چکیده
منابع مشابه
Friction stir welding of dissimilar joint of aluminum alloy 5083 and commercially pure titanium
In this study, commercially pure titanium and aluminum alloy 5083 in connection rotational speed of 1120 rpm and a feed rate of 50 mm per minute for butt welding by friction stir welding has been successfully completed. Micro-structure, hardness and tensile test was conducted on the connection. Welding area is a composite of aluminum and titanium particles that the particles plays an important ...
متن کاملFriction stir welding of dissimilar joint of aluminum alloy 5083 and commercially pure titanium
In this study, commercially pure titanium and aluminum alloy 5083 in connection rotational speed of 1120 rpm and a feed rate of 50 mm per minute for butt welding by friction stir welding has been successfully completed. Micro-structure, hardness and tensile test was conducted on the connection. Welding area is a composite of aluminum and titanium particles that the particles plays an important ...
متن کاملAnalysis and Comparison of Friction Stir Welding and Laser Assisted Friction Stir Welding of Aluminum Alloy
Friction Stir Welding (FSW) is a solid-state joining process; i.e., no melting occurs. The welding process is promoted by the rotation and translation of an axis-symmetric non-consumable tool along the weld centerline. Thus, the FSW process is performed at much lower temperatures than conventional fusion welding, nevertheless it has some disadvantages. Laser Assisted Friction Stir Welding (LAFS...
متن کاملForming and Properties of Friction Stir Welding Process for Dissimilar Mg Alloy
For hot extrusions of magnesium alloy sheets, Dissimilar AZ80 and AZ31 were used, in which AZ80 was placed on advancing side and AZ31 on retreating side, using friction stir butt welding with different process parameters. Some defect-free welded joints with good weld surfaces could be obtained with some suitable welding conditions. The maximum tensile strength of welded joint which is 225.5 MPa...
متن کاملEnhanced superplasticity in commercially pure titanium alloy
The superplasticity of commercially pure titanium alloy at high temperature was studied and the dynamic recrystallization phenomenon of the alloy was investigated by using electron back scattered diffraction. A two-step deformation method was used to increase the ductility of the alloy from 188% to 243%. 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of FAMENA
سال: 2017
ISSN: 1333-1124,1849-1391
DOI: 10.21278/tof.41107