Friction and Wear Characteristics of the Resin Bonded Solid Lubricant Films (PTFE and MoS2 as Solid Lubricant)
نویسندگان
چکیده
منابع مشابه
Wear resistant solid lubricant coating made from PTFE and epoxy
A composite coating of polytetrafluoroethylene and epoxy shows 100 · improvements in wear resistance as compared to either of its constituents alone and reduced friction coefficient under testing on a pin-on-disk tribometer. This coating is made by impregnating an expanded PTFE film with epoxy, which provides three unique functions: (1) the epoxy compartmentalizes the PTFE nodes, which is belie...
متن کاملCryogenic friction behavior of PTFE based solid lubricant composites
Solid lubricants used in aerospace applications must provide low friction and a predictable operation life over an extreme range of temperatures, environments and contact conditions. PTFE and PTFE composites have shown favorable tribological performance as solid lubricants. This study evaluates the effect of temperature on the friction coefficient of neat PTFE, a PTFE/ PEEK composite and an exp...
متن کاملSolid lubricant behavior of MoS2 and WSe2-based nanocomposite coatings
Tribological coatings made of MoS2 and WSe2 phases and their corresponding combinations with tungsten carbide (WC) were prepared by non-reactive magnetron sputtering of individual targets of similar composition. A comparative tribological analysis of these multiphase coatings was done in both ambient air (30-40% relative humidity, RH) and dry nitrogen (RH<7%) environments using the same tribome...
متن کاملTribological behavior of sputter-deposited MoSX/Ni coatings
AbstractSputtered MoS2 coatings have been mostly used as a solid lubricant. In this investigation, MoSx/Ni composite coatings with Ni contents varying from 0 to 22 % were deposited onto steel substrate using a DC magnetron sputter process. The MoS2/Ni ratio in the coatings was controlled by sputtering the composite targets. The composition, microstructure, and mechanical properties of the...
متن کاملNanostructure of Au-20%Pd layers in MoS2 multilayer solid lubricant films
High-resolution electron microscopy imaging and electron and X-ray diffraction techniques have been used to characterize the structure of low and high flux Au-20%Pd layers in Au-20%Pd/MoS2 multilayer solid lubricant thin films. Images clearly reveal different morphologies for the metal layers in the two flux regimes, which can be correlated to the variation in fracture resistance reported by an...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series C
سال: 2004
ISSN: 0387-5024,1884-8354
DOI: 10.1299/kikaic.70.283